Borealis Daplen™ FS65T20 Polypropylene Compound 20% Mineral Filled, Detergent Resistant

Category Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer Borealis
Trade Name Daplen™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis Daplen™ FS65T20 Polypropylene Compound 20% Mineral Filled, Detergent Resistant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Daplen FS65T20 is a 20% mineral filled polypropylene compound intended for injection molding. FS65T20 has been developed especially for applications requiring high detergent resistance and heat stability. FS65T20 has well balanced mechanical properties, medium flow rate and good processability and its tested and approved according to UL94 HB. Daplen FS65T20 has been developed for washing machine parts, dishwasher components, and household appliances.Information provided by the Manufacturer.
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0090 cm/cm
0.0090 in/in
150x80x20
Linear Mold Shrinkage, Transverse 0.010 cm/cm
0.010 in/in
150x80x20; Borealis Method
Melt Flow 6.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
6.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
26 g/10 min

@Load 5.00 kg,
Temperature 230 °C
26 g/10 min

@Load 11.0 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 82.0 MPa
11900 psi
H385/30; ISO 2039
Tensile Strength, Yield 32.00 MPa
4641 psi
At 50 mm/min; ISO 527-2
Elongation at Yield 4.9 %
4.9 %
At 50 mm/min; ISO 527-2
Flexural Modulus 2.80 GPa
406 ksi
At 5 mm/min; ISO 178
Charpy Impact Unnotched 4.30 J/cm²
20.5 ft-lb/in²
ISO 179/1eU
1.40 J/cm²

@Temperature -20.0 °C
6.66 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eU
Charpy Impact, Notched 0.230 J/cm²
1.09 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 121 °C
250 °F
ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi) 60.0 °C
140 °F
ISO 75-2
Vicat Softening Point 89.0 °C
192 °F
B (50N); ISO 306
154 °C
309 °F
A (10N); ISO 306
Processing Properties Metric English Comments
Melt Temperature 210 - 260 °C
410 - 500 °F
Polymer Mass Temp
Mold Temperature 30.0 - 60.0 °C
86.0 - 140 °F