Borealis Daplen™ EF103AE Polypropylene TPO Compound

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Mica Filler , Polypropylene, Mineral Reinforced
Manufacturer Borealis
Trade Name Daplen™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis Daplen™ EF103AE Polypropylene TPO Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Daplen™ EF103AE is a 10% mineral filled elastomer modified polypropylene compound intended for injection molding. This material has excellent balanced mechanical properties, high melt flow rate and gives a good surface quality. Applications: Daplen™ EF103AE has been developed especially for the car industry to be used in automotive exterior parts including bumpers, body side moldings, and body panels.Information provided by Borealis AG
Physical Properties Metric English Comments
Density 0.970 g/cc
0.0350 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0010 cm/cm
0.0010 in/in
post shrinkage; 2 hours, 90°C
0.0085 cm/cm
0.0085 in/in
mold average;Borealis Method
Melt Flow 16 g/10 min

@Load 2.16 kg,
Temperature 230 °C
16 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 18.0 MPa
2610 psi
50mm/min; ISO 527-2
Elongation at Break >= 100 %
>= 100 %
50mm/min; ISO 527-2
Elongation at Yield 8.0 %
8.0 %
50mm/min; ISO 527-2
Tensile Modulus 1.20 GPa
174 ksi
1mm/min; ISO 527-2
Flexural Strength 22.0 MPa
3190 psi
ISO 178
Flexural Modulus 1.20 GPa
174 ksi
2mm/min; ISO 178
Izod Impact, Notched (ISO) 6.50 kJ/m²

@Temperature -20.0 °C
3.09 ft-lb/in²

@Temperature -4.00 °F
ISO 180/1A
44.0 kJ/m²

@Temperature 23.0 °C
20.9 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1A
Charpy Impact Unnotched 21.0 J/cm²

@Temperature -20.0 °C
99.9 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eU
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.540 J/cm²

@Temperature -30.0 °C
2.57 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
0.660 J/cm²

@Temperature -20.0 °C
3.14 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eA
4.60 J/cm²

@Temperature 23.0 °C
21.9 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear 80.0 µm/m-°C

@Temperature -30.0 - 80.0 °C
44.4 µin/in-°F

@Temperature -22.0 - 176 °F
Borealis Method
Deflection Temperature at 0.46 MPa (66 psi) 83.0 °C
181 °F
ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi) 48.0 °C
118 °F
ISO 75-2
Vicat Softening Point 40.0 °C

@Load 5.10 kg
104 °F

@Load 11.2 lb
ISO 306
Processing Properties Metric English Comments
Processing Temperature 220 - 260 °C
428 - 500 °F
mass temperature
Feed Temperature 40.0 - 80.0 °C
104 - 176 °F
Mold Temperature 30.0 - 50.0 °C
86.0 - 122 °F
Injection Velocity 100 - 200 mm/sec
3.94 - 7.87 in/sec
Hold Pressure 30.0 - 60.0 MPa
4350 - 8700 psi
Descriptive Properties Value Comments
Back Pressure low to medium
Screw Speed low to medium