Borealis Daplen™ EE137AI Polypropylene Compound 10% Mineral Filled

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced
Manufacturer Borealis
Trade Name Daplen™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis Daplen™ EE137AI Polypropylene Compound 10% Mineral Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Daplen EE137AI is a 10% mineral filled grade intended for injection molding. EE137AI has been developed especially for the car industry, to be used in interior parts where high scratch resistance is a necessity. EE138AI offers good balance in stiffness/impact strength and has very good scratch resistance.Daplen EE137AI has been developed especially for dashboards, pillar trims, door panels and pockets, and other automotive interior parts.Information provided by the Manufacturer.
Physical Properties Metric English Comments
Density 0.960 g/cc
0.0347 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0011 cm/cm
0.0011 in/in
Borealis Method
Melt Flow 12 g/10 min

@Load 2.16 kg,
Temperature 230 °C
12 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
45 g/10 min

@Load 5.00 kg,
Temperature 230 °C
45 g/10 min

@Load 11.0 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 42.0 MPa
6090 psi
H385/30; ISO 2039
Tensile Strength, Yield 20.99 MPa
3045 psi
At 50 mm/min; ISO 527-2
Elongation at Yield 6.0 %
6.0 %
At 50 mm/min; ISO 527-2
Tensile Modulus 1.85 GPa
268 ksi
At 1 mm/min; ISO 527-2
Flexural Modulus 1.70 GPa
247 ksi
At 2 mm/min; ISO 178
Izod Impact, Notched (ISO) 25.0 kJ/m²
11.9 ft-lb/in²
ISO 180/1A
5.00 kJ/m²

@Temperature 0.000 °C
2.38 ft-lb/in²

@Temperature 32.0 °F
ISO 180/1A
Charpy Impact Unnotched 16.0 J/cm²
76.1 ft-lb/in²
ISO 179/1eU
6.00 J/cm²

@Temperature -20.0 °C
28.6 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eU
Charpy Impact, Notched 2.00 J/cm²
9.52 ft-lb/in²
ISO 179/1eA
0.450 J/cm²

@Temperature -20.0 °C
2.14 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 100 °C
212 °F
ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi) 55.0 °C
131 °F
ISO 75-2
Vicat Softening Point 54.0 °C
129 °F
B (50N); ISO 306
136 °C
277 °F
A (10N); ISO 306
Processing Properties Metric English Comments
Melt Temperature 220 - 260 °C
428 - 500 °F
Mold Temperature 30.0 - 50.0 °C
86.0 - 122 °F