Borealis Borstar® FB3450 HDPE for Film Extrusion

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE
Manufacturer Borealis
Trade Name Borstar®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis Borstar® FB3450 HDPE for Film Extrusion.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Borstar® FB3450 is a high density polyethylene. Borstar® FB3450 is well suited for multilayer coextruded films where higher stiffness and toughness than in standard LDPE and LLDPE is required. Applications: Borstar® FB3450 has been developed especially for applications like blending, and general packaging filmInformation provided by Borealis AG
Physical Properties Metric English Comments
Density 0.945 g/cc
0.0341 lb/in³
ISO 1183
Melt Flow 0.30 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.30 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
1.2 g/10 min

@Load 5.00 kg,
Temperature 190 °C
1.2 g/10 min

@Load 11.0 lb,
Temperature 374 °F
ISO 1133
25 g/10 min

@Load 21.6 kg,
Temperature 190 °C
25 g/10 min

@Load 47.6 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 100 %
100 %
ISO 527-3
Film Elongation at Break, TD 390 %
390 %
ISO 527-3
Tensile Modulus 0.290 GPa
42.1 ksi
MD; ASTM D882-A
0.340 GPa
49.3 ksi
TD; ASTM D882-A
Dart Drop, Total Energy 2.10 J
1.55 ft-lb
74N; ASTM D5748
Coefficient of Friction 0.50
0.50
ISO 8295
Dart Drop Test 100 g
0.221 lb
ISO 7765-1
Film Tensile Strength at Break, MD 44.0 MPa
6380 psi
ISO 527-3
Film Tensile Strength at Break, TD 26.0 MPa
3770 psi
ISO 527-3
Thermal Properties Metric English Comments
Melting Point 128 °C
262 °F
ISO 11357-3
Vicat Softening Point 123 °C
253 °F
ISO 306
Optical Properties Metric English Comments
Haze 24 %
24 %
ASTM D1003
Gloss 40 %
40 %
ASTM D2457