Borealis Bormod™ HC904CF Polypropylene

Category Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer Borealis
Trade Name Bormod™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis Bormod™ HC904CF Polypropylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Bormod™ BJ368MO is a polypropylene copolymer characterized by good flow, and optimum combination of high stiffness and high impact strength. The material is nucleated with Borstar® Nucleation Technology (BNT). Flow properties, nucleation and good stiffness give potential for cycle time reduction. The material have good antistatic performance and good mould release properties. Applications: Thin wall containers.Information provided by Borealis AG
Physical Properties Metric English Comments
Density 0.905 g/cc
0.0327 lb/in³
ISO 1183
Melt Flow 2.8 g/10 min

@Load 2.16 kg,
Temperature 230 °C
2.8 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 39.5 MPa
5730 psi
50mm/min; ISO 527-2
Film Elongation at Break, MD 158 %
158 %
blown films; ISO 527-3
450 %
450 %
cast films; ISO 527-3
Film Elongation at Break, TD 4.0 %
4.0 %
blown films; ISO 527-3
5.0 %
5.0 %
cast films; ISO 527-3
Elongation at Yield 7.0 %
7.0 %
ISO 527-2
Tensile Modulus 1.55 GPa
225 ksi
roll stack films TD; ISO 527-3
1.70 GPa
247 ksi
roll stack films MD; ISO 527-3
1.70 GPa
247 ksi
cast films TD; ISO 527-3
1.875 GPa
271.9 ksi
cast films MD; ISO 527-3
2.05 GPa
297 ksi
blown films MD; ISO 527-3
2.07 GPa
300 ksi
blown films TD; ISO 527-3
Flexural Modulus 2.00 GPa
290 ksi
50% humidity; ISO 178
Charpy Impact, Notched 0.400 J/cm²

@Temperature 23.0 °C
1.90 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Dart Drop, Total Energy 1.00 J

@Thickness 0.0500 mm
0.738 ft-lb

@Thickness 0.00197 in
cast films; ISO 7765-2
1.00 J

@Thickness 0.300 mm
0.738 ft-lb

@Thickness 0.0118 in
roll stack films; ISO 7765-2
Coefficient of Friction 0.30 - 0.40
0.30 - 0.40
film to film; cast; ISO 8295
0.30 - 0.40
0.30 - 0.40
film to film;blown; ISO 8295
Dart Drop Test >= 25.0 g

@Thickness 0.0500 mm
>= 0.0551 lb

@Thickness 0.00197 in
blown films; ISO 7765-1
Film Tensile Strength at Break, MD 42.0 MPa
6090 psi
blown films; ISO 527-3
60.0 MPa
8700 psi
cast films; ISO 527-3
Film Tensile Strength at Break, TD 40.0 MPa
5800 psi
cast films; ISO 527-3
42.0 MPa
6090 psi
blown films; ISO 527-3
Thermal Properties Metric English Comments
Melting Point 166 °C
331 °F
DSC; ISO 3146
Deflection Temperature at 0.46 MPa (66 psi) 118 °C
244 °F
ISO 75-2
Vicat Softening Point 156 °C

@Load 1.02 kg
313 °F

@Load 2.25 lb
A50; ISO 306
Optical Properties Metric English Comments
Haze <= 5.0 %
<= 5.0 %
cast films; ASTM D1003
<= 13.5 %
<= 13.5 %
roll stack films; ASTM D1003
<= 14 %
<= 14 %
blown films; ASTM D1003
Gloss >= 45 %
>= 45 %
20° of arc, blown films; ASTM D2457
>= 110 %
>= 110 %
20° of arc, cast films; ASTM D2457
>= 130 %
>= 130 %
20° of arc, roll stack films; ASTM D2457