Borealis Bormod™ BJ368MO Polypropylene Heteroplastic Copolymer for Injection Molding

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer
Manufacturer	Borealis
Trade Name	Bormod™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Borealis Bormod™ BJ368MO Polypropylene Heteroplastic Copolymer for Injection Molding.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Bormod™ BJ368MO is a polypropylene copolymer characterized by good flow, and optimum combination of high stiffness and high impact strength. The material is nucleated with Borstar® Nucleation Technology (BNT). Flow properties, nucleation and good stiffness give potential for cycle time reduction. The material have good antistatic performance and good mould release properties. Applications: Thin wall containers.Information provided by Borealis AG

Physical Properties	Metric	English	Comments
Density	0.903 g/cc	0.0326 lb/in³	ISO 1183
Melt Flow	70 g/10 min @Load 2.16 kg, Temperature 230 °C	70 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	86	86	ISO 2039-2
Tensile Strength, Yield	25.0 MPa	3630 psi	50mm/min; ISO 527-2
Elongation at Yield	4.0 %	4.0 %	50mm/min; ISO 527-2
Tensile Modulus	1.45 GPa	210 ksi	ISO 527-2
Charpy Impact, Notched	0.400 J/cm² @Temperature -20.0 °C	1.90 ft-lb/in² @Temperature -4.00 °F	ISO 179/1eA
	0.550 J/cm² @Temperature 23.0 °C	2.62 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	102 °C	216 °F	ISO 75-2

Processing Properties	Metric	English
Melt Temperature	210 - 260 °C	410 - 500 °F
Mold Temperature	10.0 - 30.0 °C	50.0 - 86.0 °F
Hold Pressure	20.0 - 50.0 MPa	2900 - 7250 psi

Descriptive Properties	Value	Comments
Injection Velocity	high