Borealis Bormed™ HE2581-PH HDPE for Healthcare Applications

Category	Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Blow Molding Grade
Manufacturer	Borealis
Trade Name	Bormed™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Borealis Bormed™ HE2581-PH HDPE for Healthcare Applications.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Bormed HE2581-PH is a high-density polyethylene intended for blow molding of products with high stiffness and very good environmental stress crack resistance (ESCR). Bormed HE2581-PH can as well be used to produce products via IBM or ISBM. Bormed HE2581-PH is recommended for bottles and containers up to 10 liters.Bormed HE2581-PH is designed for Pharmaceutical and diagnostic packaging, packaging for dialyze liquid, and containers for fine chemicals.Information provided by the Manufacturer.

Physical Properties	Metric	English	Comments
Density	0.958 g/cc	0.0346 lb/in³	ISO 1183
ESCR 10% Igepal®	>= 100 hour	>= 100 hour	ASTM D1693
Melt Flow	0.30 g/10 min @Load 2.16 kg, Temperature 190 °C	0.30 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
	1.3 g/10 min @Load 5.00 kg, Temperature 190 °C	1.3 g/10 min @Load 11.0 lb, Temperature 374 °F	ISO 1133
High Load Melt Index	28 g/10 min @Load 21.6 kg, Temperature 190 °C	28 g/10 min @Load 47.6 lb, Temperature 374 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	65	65	ISO 868
Tensile Strength, Yield	29.0 MPa	4210 psi	At 50 mm/min; ISO 527-2
Elongation at Yield	8.0 %	8.0 %	At 50 mm/min; ISO 527-2
Tensile Modulus	1.30 GPa	189 ksi	At 1 mm/min; ISO 527-2
Flexural Modulus	1.40 GPa	203 ksi	At 1 mm/min; ISO 178

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	80.0 °C	176 °F	ISO 75-2