Borealis BS2581 High Density Polyethylene for Blow Molding

Category	Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Blow Molding Grade
Manufacturer	Borealis
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Borealis BS2581 High Density Polyethylene for Blow Molding.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

BS2581 is a high density polyethylene intended for blow molding products with high stiffness and very good environmental stress crack resistance (ESCR). Applications: industrial chemicals, household and chemical containers such as detergents, cleaners, motor oils, and other bottles and containers up to 10 liters.Information provided by Borealis AG

Physical Properties	Metric	English	Comments
Density	0.958 g/cc	0.0346 lb/in³	ISO 1183
Environmental Stress Crack Resistance	100 hour	100 hour	Antarox 10%, F50; ASTM D1693-A
Melt Flow	0.30 g/10 min @Load 2.16 kg, Temperature 190 °C	0.30 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
	1.3 g/10 min @Load 5.00 kg, Temperature 190 °C	1.3 g/10 min @Load 11.0 lb, Temperature 374 °F	ISO 1133
	28 g/10 min @Load 21.6 kg, Temperature 190 °C	28 g/10 min @Load 47.6 lb, Temperature 374 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	65	65	ISO 868
Tensile Strength, Yield	29.0 MPa	4210 psi	50mm/min; ISO 527-2
Elongation at Yield	8.0 %	8.0 %	50mm/min; ISO 527-2
Tensile Modulus	1.30 GPa	189 ksi	1mm/min; ISO 527-2
Flexural Modulus	1.40 GPa	203 ksi	1mm/min; ISO 178

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	80.0 °C	176 °F	ISO 75-2

Processing Properties	Metric	English
Middle Barrel Temperature	170 - 190 °C	338 - 374 °F
Die Temperature	175 - 190 °C	347 - 374 °F
Melt Temperature	170 - 200 °C	338 - 392 °F