Borealis BE50-7032 Polypropylene Homopolymer for Non-Pressure pipes and extruded sheets

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Extrusion Grade
Manufacturer Borealis
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis BE50-7032 Polypropylene Homopolymer for Non-Pressure pipes and extruded sheets.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
BE50-7032 is a high molecular weight, low melt flow rate polypropylene homopolymer characterized by high stiffness, high heat distortion temperature and high resistance to thermal aging. The material is colored grey based on RAL 7032. Applications: BE50-7032 is recommended for non-pressure pipes and fittings, extruder sheets, solid rods, filter plates and other extrusion applications, industrial, non-pressure pipe systems, sheets and profiles.Information provided by Borealis AG
Physical Properties Metric English Comments
Density 0.905 g/cc
0.0327 lb/in³
ISO 1183
Melt Flow 0.30 g/10 min

@Load 2.16 kg,
Temperature 230 °C
0.30 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
0.60 g/10 min

@Load 5.00 kg,
Temperature 190 °C
0.60 g/10 min

@Load 11.0 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 36.0 MPa
5220 psi
50mm/min; ISO 527-2
Elongation at Yield 10 %
10 %
50mm/min; ISO 527-2
Tensile Modulus 1.65 GPa
239 ksi
1mm/min; ISO 527-2
Charpy Impact, Notched 0.200 J/cm²

@Temperature -20.0 °C
0.952 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eA
0.700 J/cm²

@Temperature 23.0 °C
3.33 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Vicat Softening Point 95.0 °C

@Load 5.10 kg
203 °F

@Load 11.2 lb
B50; ISO 306
Processing Properties Metric English Comments
Middle Barrel Temperature 190 - 230 °C
374 - 446 °F
cylinder
Die Temperature 200 - 230 °C
392 - 446 °F
Melt Temperature 200 - 230 °C
392 - 446 °F
Head Temperature 200 - 230 °C
392 - 446 °F