Borealis BA11CF Polypropylene Copolymer

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer
Manufacturer	Borealis
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Borealis BA11CF Polypropylene Copolymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

BA110CF is a heterophasic copolymer. This grade is suitable for use on chill roll processes. This grade is suitable for the manufacturing of unoriented films on cast and tubular quench film lines. Applications: BA110CF is recommended for food packaging, lamination films, stationary films, monoaxial oriented films, and inner layer in co extrusion.Information provided by Borealis AG

Physical Properties	Metric	English	Comments
Density	0.900 - 0.910 g/cc	0.0325 - 0.0329 lb/in³	ISO 1183
Melt Flow	0.85 g/10 min @Load 2.16 kg, Temperature 230 °C	0.85 g/10 min @Load 4.76 lb, Temperature 446 °F	50% relative humidity; ISO 1133

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	550 - 750 %	550 - 750 %	ISO 527-3
Film Elongation at Break, TD	550 - 750 %	550 - 750 %	ISO 527-3
Tensile Modulus	0.500 - 0.600 GPa	72.5 - 87.0 ksi	MD/TD; ISO 527-3
Flexural Modulus	1.20 GPa	174 ksi	ISO 178
Dart Drop, Total Energy	25.0 J @Thickness 0.0500 mm	18.4 ft-lb @Thickness 0.00197 in	1100 N force; ISO 7765-2
Film Tensile Strength at Break, MD	40.0 - 60.0 MPa	5800 - 8700 psi	ISO 527-3
Film Tensile Strength at Break, TD	30.0 - 50.0 MPa	4350 - 7250 psi	ISO 527-3

Thermal Properties	Metric	English	Comments
Melting Point	158 - 162 °C	316 - 324 °F	50% humidity, 23°C; ISO 3146
Vicat Softening Point	150 °C @Load 1.02 kg	302 °F @Load 2.25 lb	50% humidity, 23°C; ISO 306

Optical Properties	Metric	English	Comments
Haze	<= 40 %	<= 40 %	ASTM D1003
Gloss	>= 3.0 %	>= 3.0 %	ASTM D2457