Bond Laminates TEPEX® dynalite 108-FGAL290(2)-FG290(x)/45% Filament Glass – TPU Consolidated Composite Laminate

Category Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Glass Fiber Reinforced
Manufacturer Bond Laminates
Trade Name TEPEX® dynalite
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Bond Laminates TEPEX® dynalite 108-FGAL290(2)-FG290(x)/45% Filament Glass – TPU Consolidated Composite Laminate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Within the TEPEX® composite laminate, TPU distinguishes itself from alternative resin systems by its specific physical properties. The TPU resin is tough which results in an excellent impact and easy to mold, obtaining an excellent surface quality. The TPU-glass laminates can easily be bonded with common adhesive systems. An excellent adhesion is achieved when over molding with injection molding TPU grades.Typical application environments are sporting goods applications, helmet shells, cosmetic applications, footwear.Information provided by Bond Laminates, GmbH.
Physical Properties Metric English Comments
Density 1.82 g/cc
0.0658 lb/in³
Filler Content 45 %
45 %
by volume
Mechanical Properties Metric English Comments
Tensile Strength 405 MPa
58700 psi
transverse; ISO 527-4/5
430 MPa
62400 psi
longitudinal; ISO 527-4/5
Elongation at Break 2.9 %
2.9 %
longitudinal; ISO 527-4/5
2.9 %
2.9 %
transverse; ISO 527-4/5
Tensile Modulus 23.5 GPa
3410 ksi
transverse; ISO 527-4/5
25.0 GPa
3630 ksi
longitudinal; ISO 527-4/5
Flexural Strength 550 MPa
79800 psi
transverse; ISO 178
585 MPa
84800 psi
longitudinal; ISO 178
Flexural Modulus 21.0 GPa
3050 ksi
transverse; ISO 178
21.5 GPa
3120 ksi
longitudinal; ISO 178
Thermal Properties Metric English Comments
Melting Point 190 °C
374 °F
DSC 3146
Maximum Service Temperature, Air 90.0 °C

@Time 7.20e+7 sec
194 °F

@Time 20000 hour
Relative Temperature Index; IEC 216/1
Deflection Temperature at 1.8 MPa (264 psi) 185 °C
365 °F
ISO 75-1/2
Minimum Service Temperature, Air -30.0 °C
-22.0 °F
Processing Properties Metric English Comments
Processing Temperature 210 - 230 °C
410 - 446 °F
Descriptive Properties Value Comments
Reinforcement Area weight
290 g/m²
Fabric
twill 2/2
Fibers
filament glass (outer fibers coated with aluminum)
Weight Rate
50% longitudinal and transverse
Yarn
3x68 tex longitudinal and transverse