Bond Laminates TEPEX® dynalite 102-RG600(x)/47% Roving Glass – PA 6 Consolidated Composite Laminate

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled
Manufacturer Bond Laminates
Trade Name TEPEX® dynalite
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Bond Laminates TEPEX® dynalite 102-RG600(x)/47% Roving Glass – PA 6 Consolidated Composite Laminate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Within the TEPEX® composite laminate, Polyamide 6 is a resin known for its toughness, stiffness, abrasion resistance, heat and chemical resistances. Roving E-Glass fibers have an excellent impact performance. This makes the composite material tough and fatigue resistant while offering excellent mechanical properties.Typical application environments are within automotive applications, large structural parts, bumper systems, structural sporting goods applications, helmet shells.Information provided by Bond Laminates, GmbH.
Physical Properties Metric English Comments
Density 1.80 g/cc
0.0650 lb/in³
Filler Content 47 %
47 %
by volume
Thickness 500 microns
19.7 mil
laminate layer thickness
Mechanical Properties Metric English Comments
Tensile Strength 390 MPa
56600 psi
transverse; ISO 527-4/5
404 MPa
58600 psi
longitudinal; ISO 527-4/5
Elongation at Break 2.2 %
2.2 %
longitudinal; ISO 527-4/5
2.2 %
2.2 %
transverse; ISO 527-4/5
Tensile Modulus 21.5 GPa
3120 ksi
transverse; ISO 527-4/5
22.4 GPa
3250 ksi
longitudinal; ISO 527-4/5
Flexural Strength 585 MPa
84800 psi
transverse; ISO 178
620 MPa
89900 psi
longitudinal; ISO 178
Flexural Modulus 18.7 GPa
2710 ksi
transverse; ISO 178
19.2 GPa
2780 ksi
longitudinal; ISO 178
Poissons Ratio 0.17
0.17
longitudinal; ISO 527-4/5
0.17
0.17
transverse; ISO 527-4/5
Charpy Impact Unnotched 14.5 J/cm²
69.0 ft-lb/in²
longitudinal; ISO 179/1eU
Thermal Properties Metric English Comments
CTE, linear 15.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
8.33 µin/in-°F

@Temperature 73.4 - 176 °F
longitudinal; ASTM E831
15.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
8.33 µin/in-°F

@Temperature 73.4 - 176 °F
transverse; ASTM E831
19.0 µm/m-°C

@Temperature -30.0 - 23.0 °C
10.6 µin/in-°F

@Temperature -22.0 - 73.4 °F
longitudinal; ASTM E831
19.0 µm/m-°C

@Temperature -30.0 - 23.0 °C
10.6 µin/in-°F

@Temperature -22.0 - 73.4 °F
transverse; ASTM E831
Melting Point 220 °C
428 °F
DSC 3146
Maximum Service Temperature, Air 120 °C

@Time 7.20e+7 sec
248 °F

@Time 20000 hour
Relative Temperature Index; IEC 216/1
Deflection Temperature at 1.8 MPa (264 psi) 215 °C
419 °F
ISO 75-1/2
Minimum Service Temperature, Air -30.0 °C
-22.0 °F
Glass Transition Temp, Tg 60.0 °C
140 °F
DSC 3146
Processing Properties Metric English Comments
Processing Temperature 240 - 260 °C
464 - 500 °F
Descriptive Properties Value Comments
Reinforcement Area weight
600 g/m²
Fabric
twill
Fibers
roving glass
Weight Rate
50% longitudinal and transverse
Yarn
1200 tex longitudinal and transverse