Bhansali Engineering Abstron MIF-35 ABS Injection Molding Grade
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | Bhansali Engineering |
| Trade Name | Abstron |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Bhansali Engineering Abstron MIF-35 ABS Injection Molding Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High Impact, Medium, High Flow, General PurposeInformation provided by Bhansali
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.045 g/cc | 0.03775 lb/in³ | ASTM D-792 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM D-955 |
| Melt Flow | 38 g/10 min @Load 10.0 kg, Temperature 220 °C |
38 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D-1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 110 | 110 | ASTM D-785 |
| Tensile Strength, Yield | 44.1 MPa @Thickness 3.20 mm |
6400 psi @Thickness 0.126 in |
Type 1; ASTM D638 |
| Flexural Yield Strength | 63.7 MPa @Thickness 6.40 mm |
9250 psi @Thickness 0.252 in |
ASTM D790 |
| Flexural Modulus | 2.16 GPa @Thickness 6.40 mm |
313 ksi @Thickness 0.252 in |
ASTM D790 |
| Izod Impact, Notched | 2.16 J/cm @Thickness 6.40 mm |
4.04 ft-lb/in @Thickness 0.252 in |
ASTM D256 |
| 2.549 J/cm @Thickness 3.20 mm |
4.775 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C | 199 °F | Method A - Annealed; ASTM D-648 |
| Vicat Softening Point | 103 °C | 217 °F | Method B; ASTM D-1525 |
| Flammability, UL94 | HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
UL-94 |