Beijing Chemical Industry KAIFA® MN101 Nylon 66 Resin

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade
Manufacturer Beijing Chemical Industry Research Institute (Group)
Trade Name KAIFA®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Beijing Chemical Industry KAIFA® MN101 Nylon 66 Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Good flow, High impactInformation provided by Beijing Chemical Industry Research Institute (Group)
Physical Properties Metric English Comments
Density 1.10 g/cc
0.0397 lb/in³
ASTM D792
Linear Mold Shrinkage 0.014 - 0.018 cm/cm
0.014 - 0.018 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 60.0 MPa
8700 psi
ASTM D638
Flexural Strength 91.0 MPa
13200 psi
ASTM D790
Charpy Impact Unnotched 12.0 J/cm²
57.1 ft-lb/in²
ISO179
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
ISO179
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 75.0 °C
167 °F
ASTM D648
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+14 ohm-cm
1.00e+14 ohm-cm
ASTM D257
Dielectric Constant 2.9

@Frequency 1e+6 Hz
 2.9

@Frequency 1e+6 Hz
 ASTM D150
Dielectric Strength 30.0 kV/mm

@Thickness 2.00 mm
 762 kV/in

@Thickness 0.0787 in
 ASTM D149
Dissipation Factor 0.020

@Frequency 1e+6 Hz
 0.020

@Frequency 1e+6 Hz
 ASTM D150
Processing Properties Metric English Comments
Rear Barrel Temperature 220 - 265 °C
428 - 509 °F
Middle Barrel Temperature 260 - 265 °C
500 - 509 °F
Front Barrel Temperature 260 - 270 °C
500 - 518 °F
Nozzle Temperature 260 - 265 °C
500 - 509 °F
Mold Temperature 60.0 - 90.0 °C
140 - 194 °F
Drying Temperature 130 °C
266 °F
Dry Time 4 hour
4 hour
Injection Pressure 60.0 - 100 MPa
8700 - 14500 psi