Barlog Plastics KEBAFORM C 902 UR POM Copolymer unreinforced, impact modified
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Impact Modified |
| Manufacturer | Barlog Plastics |
| Trade Name | KEBAFORM |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Barlog Plastics KEBAFORM C 902 UR POM Copolymer unreinforced, impact modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
POM-IInformation provided by BARLOG plastics GmbH.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.018 cm/cm | 0.018 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.018 cm/cm | 0.018 in/in | ISO 294-4 |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | ISO 527-1 |
| Elongation at Yield | 14 % | 14 % | ISO 527-1 |
| Tensile Modulus | 2.05 GPa | 297 ksi | ISO 527-1 |
| Charpy Impact Unnotched | NB | NB | ISO 179-1eU |
| Charpy Impact, Notched | 1.10 J/cm² | 5.23 ft-lb/in² | ISO 179-1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 166 °C | 331 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB | HB | IEC 60695-11-10 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Resin Type | POM-I |