Barlog Plastics KEBAFORM C 90.0 POM Copolymer unreinforced

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced
Manufacturer Barlog Plastics
Trade Name KEBAFORM
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Barlog Plastics KEBAFORM C 90.0 POM Copolymer unreinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
POMInformation provided by BARLOG plastics GmbH.
Physical Properties Metric English Comments
Density 1.41 g/cc
0.0509 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.22 %
0.22 %
similar to ISO 62 test
Linear Mold Shrinkage, Flow 0.020 cm/cm
0.020 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.020 cm/cm
0.020 in/in
ISO 294-4
Melt Flow 9.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
9.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 64.0 MPa
9280 psi
ISO 527-1
Elongation at Yield 9.0 %
9.0 %
ISO 527-1
Tensile Modulus 2.70 GPa
392 ksi
ISO 527-1
Charpy Impact Unnotched NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179-1eU
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179-1eU
Charpy Impact, Notched 0.700 J/cm²
3.33 ft-lb/in²
ISO 179-1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 120 µm/m-°C
66.7 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 120 µm/m-°C
66.7 µin/in-°F
ISO 11359-1/-2
Melting Point 166 °C
331 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 160 °C
320 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 110 °C
230 °F
ISO 75-1/-2
Flammability, UL94 HB

@Thickness 0.800 mm
HB

@Thickness 0.0315 in
UL Registered; IEC 60695-11-10
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
IEC 60093
Surface Resistance 1.00e+16 ohm
1.00e+16 ohm
IEC 60093
Descriptive Properties Value Comments
Resin Type POM