BNZ Materials Marinite® C Ceramic Board for Aluminum Contact

Category Ceramic , Oxide
Manufacturer BNZ Materials, Inc.
Trade Name Marinite®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BNZ Materials Marinite® C Ceramic Board for Aluminum Contact.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
These boards are heat treated formulations for use in conveying, containing and forming molten aluminum and other non-ferrous metals. Applications include holding furnace linings, tips for continuous casters, transition plates, rings, plugs, baffles, troughs, spouts, floats and filter boxes.Information provided by BNZ Materials Inc.
Physical Properties Metric English Comments
Density 0.865 g/cc
0.0312 lb/in³
Mechanical Properties Metric English Comments
Modulus of Rupture 0.00620 GPa
0.899 ksi
Compressive Yield Strength 11.0 MPa

@Strain 5.00 %
1600 psi

@Strain 5.00 %
Compressive Strength 15.2 MPa
2200 psi
ultimate load
Thermal Properties Metric English Comments
Thermal Conductivity 0.140 W/m-K

@Temperature 204 °C
0.972 BTU-in/hr-ft²-°F

@Temperature 399 °F
0.140 W/m-K

@Temperature 316 °C
0.972 BTU-in/hr-ft²-°F

@Temperature 601 °F
0.150 W/m-K

@Temperature 427 °C
1.04 BTU-in/hr-ft²-°F

@Temperature 801 °F
0.150 W/m-K

@Temperature 538 °C
1.04 BTU-in/hr-ft²-°F

@Temperature 1000 °F
Shrinkage 2.3 %

@Temperature 732 °C,
Time 86400 sec
2.3 %

@Temperature 1350 °F,
Time 24.0 hour
Length/width, Soaking Heat Changes
9.4 %

@Temperature 732 °C,
Time 86400 sec
9.4 %

@Temperature 1350 °F,
Time 24.0 hour
Thickness, Soaking Heat Changes
Component Elements Properties Metric English Comments
Loss on Ignition(%) 5.8 %

@Temperature 732 °C
5.8 %

@Temperature 1350 °F
Processing Properties Metric English Comments
Moisture Content 2.5 %
2.5 %
Descriptive Properties Value Comments
Screw Holding Strength 100 kg
at 7/8" penetration