BNZ Materials Blazecrete 3000 Dense Castable

Category Ceramic , Oxide , Aluminum Oxide
Manufacturer BNZ Materials, Inc.
Trade Name Blazecrete
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BNZ Materials Blazecrete 3000 Dense Castable.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Blazecrete 3000 is a high alumina, high strength, general purpose castable for service to 3000°F (1667°C). Used for casting burner blocks, door linings, car tops, crucible furnace linings and special shapes. High purity for special furnace atmospheres.Information provided by BNZ Materials Inc.
Physical Properties Metric English Comments
Density 2.16 g/cc
0.0781 lb/in³
Mechanical Properties Metric English Comments
Modulus of Rupture 0.00690 GPa
1.00 ksi
At Use Limit; ASTM C268
0.00210 GPa

@Temperature 815 °C
0.305 ksi

@Temperature 1500 °F
ASTM C268
0.00210 GPa

@Temperature 1095 °C
0.305 ksi

@Temperature 2003 °F
ASTM C268
0.00280 GPa

@Temperature 540 °C
0.406 ksi

@Temperature 1000 °F
Fired; ASTM C268
0.00340 GPa

@Temperature 1260 °C
0.493 ksi

@Temperature 2300 °F
ASTM C268
0.00480 GPa

@Temperature 104 °C
0.696 ksi

@Temperature 219 °F
Dried; ASTM C268
0.00550 GPa

@Temperature 1371 °C
0.798 ksi

@Temperature 2500 °F
ASTM C268
Compressive Strength 18.6 MPa

@Temperature 1095 °C
2700 psi

@Temperature 2003 °F
Cold Crush Strength
21.4 MPa

@Temperature 1260 °C
3100 psi

@Temperature 2300 °F
Cold Crush Strength
25.5 MPa

@Temperature 815 °C
3700 psi

@Temperature 1500 °F
Cold Crush Strength
49.0 MPa

@Temperature 1371 °C
7110 psi

@Temperature 2500 °F
Cold Crush Strength
63.4 MPa

@Temperature 1667 °C
9200 psi

@Temperature 3033 °F
Cold Crush Strength; At Use Limit
28.9 MPa

@Treatment Temp. 104 °C
4190 psi

@Treatment Temp. 219 °F
Cold Crush Strength; Dried 104°C
29.6 MPa

@Treatment Temp. 540 °C
4290 psi

@Treatment Temp. 1000 °F
Cold Crush Strength; Dried 104°C
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 1649 °C
3000 °F
Shrinkage 0.00 %

@Temperature 104 °C
0.00 %

@Temperature 219 °F
Permanent Linear Change; ASTM C210
-0.400 - 0.40 %

@Temperature 1260 °C
-0.400 - 0.40 %

@Temperature 2300 °F
Permanent Linear Change
0.10 %

@Temperature 540 °C
0.10 %

@Temperature 1000 °F
Permanent Linear Change; ASTM C210
0.10 %

@Temperature 815 °C
0.10 %

@Temperature 1500 °F
Permanent Linear Change; ASTM C210
0.10 %

@Temperature 1095 °C
0.10 %

@Temperature 2003 °F
Permanent Linear Change; ASTM C210
0.70 %

@Temperature 1371 °C
0.70 %

@Temperature 2500 °F
Permanent Linear Change; ASTM C210
1.0 %

@Temperature 1667 °C
1.0 %

@Temperature 3033 °F
Permanent Linear Change at Use Limit; ASTM C210
Component Elements Properties Metric English Comments
Al2O3 47.6 %
47.6 %
CaO 4.8 %
4.8 %
Fe2O3 1.8 %
1.8 %
MgO 0.20 %
0.20 %
Na2O 0.40 %
0.40 %
Includes K<sub>2</sub>O
SiO2 44 %
44 %
TiO2 1.3 %
1.3 %