BLUESTAR 101G30 PBT, 30% Glass Filled

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled
Manufacturer BLUESTAR
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BLUESTAR 101G30 PBT, 30% Glass Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Typical Applications: Appliances, molded partsInformation provided by Polymer Technology and Services, LLC (PTS).
Physical Properties Metric English Comments
Specific Gravity 1.53 g/cc
1.53 g/cc
ASTM D792
Moisture Absorption at Equilibrium 0.20 %
0.20 %
50% RH; ASTM D570
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.011 cm/cm
0.011 in/in
ASTM D955
Melt Flow 30 g/10 min

@Load 2.16 kg,
Temperature 250 °C
 30 g/10 min

@Load 4.76 lb,
Temperature 482 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 105 MPa
15200 psi
ASTM D638
Tensile Modulus 8.70 GPa
1260 ksi
ASTM D638
Flexural Strength 180 MPa
26100 psi
ASTM D790
Flexural Modulus 8.03 GPa
1160 ksi
ASTM D790
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
ASTM D256
Izod Impact, Unnotched (ISO) 62.0 kJ/m²
29.5 ft-lb/in²
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 208 °C
406 °F
ASTM D648
Flammability, UL94 HB

@Thickness 0.380 mm
 HB

@Thickness 0.0150 in
HB

@Thickness 0.800 mm
 HB

@Thickness 0.0315 in
HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
HB

@Thickness 3.20 mm
 HB

@Thickness 0.126 in