BCC Products BC 8870 Polyurethane Elastomer

Category	Polymer , Thermoset , Polyurethane, TS , Thermoset Polyurethane, Elastomer, Unreinforced , Rubber or Thermoset Elastomer (TSE)
Manufacturer	BCC Products
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BCC Products BC 8870 Polyurethane Elastomer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

BC8870 is a low viscosity two-component urethane casting compound that is specifically formulated for high abrasion and impact resistance. It is recommended for use for the production casting of highly wear-resistant parts and linings. This product is a safe, easy-to-handle, room temperature mixing and curing system that does not contain TDI, MDI, or MOCA. BC8870 is relatively insensitive to typical environmental moisture and will make good void-free parts without the problems that some conventional urethane systems exhibit.Information provided by BCC Products, Inc.

Physical Properties	Metric	English	Comments
Specific Gravity	1.10 g/cc	1.10 g/cc
Brookfield Viscosity	1800 - 2000 cP	1800 - 2000 cP	1.5 min mixed
Linear Mold Shrinkage	0.0025 cm/cm	0.0025 in/in

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	68 - 72	68 - 72
Tensile Strength, Ultimate	26.2 MPa	3800 psi	ASTM D412
Elongation at Break	400 %	400 %
Tensile Modulus	0.248 GPa	36.0 ksi
Flexural Strength	25.5 MPa	3700 psi	ASTM D790
Flexural Modulus	0.538 GPa	78.0 ksi	ASTM D790
Compressive Strength	67.6 MPa	9800 psi
Rebound	48 %	48 %	Bayshore; ASTM D575
Tear Strength	114 kN/m	650 pli	ASTM D412
Compression Set	42 %	42 %	method B; ASTM D395

Processing Properties	Metric	English	Comments
Cure Time	4320 - 7200 min	72.0 - 120 hour	full cure
	120 - 180 min @Temperature 24.0 °C	2.00 - 3.00 hour @Temperature 75.2 °F	demold time
Pot Life	18 - 20 min @Temperature 24.0 °C	18 - 20 min @Temperature 75.2 °F

Descriptive Properties	Value	Comments
Mix Ratio	100:60 by weight (Part A/Part B)