BCC Products BC 100 Thin Cyanoacrylate Adhesive
| Category | Polymer , Adhesive , Thermoset , Acrylic/Cyanoacrylate Adhesive |
| Manufacturer | BCC Products |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BCC Products BC 100 Thin Cyanoacrylate Adhesive.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
BC100 Thin is a low viscosity material ideal for bonding larger areas. BC100 Thin has a 20 second fixture cure and able to fill gaps of .002” wide. BC100 Thin is perfectly designed for bonding plastic parts and other substrates like Stainless Steel, Neoprene and ABS and even Nitrile Rubber.BONDING SCHEDULES: Stainless Steel: 10-20 seconds, ABS: 10-20 seconds, Polycarbonate: 20-40 seconds, PVC: 20-50 seconds, Neoprene: < 5 seconds, Phenolics: 10-20 seconds, PVC: < 5 seconds, Nitrile Rubber: 5 – 7 secondsInformation provided by BCC Products, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Brookfield Viscosity | 2.0 - 5.0 cP @Temperature 25.0 °C |
2.0 - 5.0 cP @Temperature 77.0 °F |
Brookfield LVF, Spindle 1-60 RPM |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Shear Strength | 3.00 - 9.03 MPa | 435 - 1310 psi | PVC; ASTM D1002/DIN 53283 |
| 5.00 - 10.0 MPa | 725 - 1450 psi | polycarbonate; ASTM D1002/DIN 53283 | |
| 10.0 - 15.0 MPa | 1450 - 2180 psi | neoprene rubber; ASTM D1002/DIN 53283 | |
| 10.0 - 15.0 MPa | 1450 - 2180 psi | etched aluminum; ASTM D1002/DIN 53283 | |
| 14.0 - 22.0 MPa | 2030 - 3190 psi | grit blasted steel; ASTM D1002/DIN 53283 | |
| 15.0 - 26.0 MPa | 2180 - 3770 psi | tensile; ASTM D1002/DIN 53283 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 162 µm/m-°C | 90.0 µin/in-°F | |
| Thermal Conductivity | 0.100 W/m-K | 0.694 BTU-in/hr-ft²-°F | ASTM C177 |
| Melting Point | 160 - 170 °C | 320 - 338 °F | |
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | |
| Minimum Service Temperature, Air | -60.0 °C | -76.0 °F | |
| Glass Transition Temp, Tg | 120 °C | 248 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 24.6 kV/mm | 625 kV/in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 0.0800 - 0.33333 min @Temperature 24.0 °C |
0.00133 - 0.0055555 hour @Temperature 75.2 °F |
|
| 1440 min @Temperature 24.0 °C |
24.0 hour @Temperature 75.2 °F |
full cure |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Gap Filling | .05mm |
Users viewing this material also viewed the following:
- Network Polymers Softflex® 7210 Black
- Ravago Manufacturing Americas Echo® RPPC 20/6 BK Polypropylene Copolymer
- Northstar Polymers PAA-109 Curing Agent
- Techmer ES Plastiblend® PA6/6,6 IM 6040 BK MB Nylon 6/66
- Lubrizol ESTANE® ETE50DT3 Ester Based Thermoplastic Polyurethane (European Grade)
- A. Schulman PAPERMATCH® H-3818 Specialty Masterbatch
- Cheng Yu Plastic PE221 Flame Retardant LDPE
- Abatron AboCoat 8709-2 A/B Carbon-Filled Electrically Conductive Epoxy Compound
- Braskem PB208 Injection Molding Low Density Polyethylene
Copyright © lookpolymers.com All Rights Reserved