BASF Ultramid® TG7S 35% Glass Filled PA6 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® TG7S 35% Glass Filled PA6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid TG7S is a 34% glass reinforced, heat stabilized, impact modified PA6 injection molding grade. It was developed to meet the demanding requirements of the first North American seat cushion pan/frame to be made of an engineering plastic as opposed to metal. TG7S exhibits improved strength,stiffness and notched impact properties over Ultramid 8333G HI.
Physical Properties Metric English Comments
Density 1.37 g/cc
0.0495 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Tensile Strength at Break 170 MPa
24700 psi
0.2 in/min; ASTM Test
77.0 MPa

@Temperature 120 °C
11200 psi

@Temperature 248 °F
ISO Data
77.0 MPa

@Temperature 120 °C
11200 psi

@Temperature 248 °F
ASTM Test
97.0 MPa

@Temperature 80.0 °C
14100 psi

@Temperature 176 °F
ASTM Test
97.0 MPa

@Temperature 80.0 °C
14100 psi

@Temperature 176 °F
ISO Data
251 MPa

@Temperature -40.0 °C
36400 psi

@Temperature -40.0 °F
ASTM Test
251 MPa

@Temperature -40.0 °C
36400 psi

@Temperature -40.0 °F
ISO Data
Tensile Strength, Ultimate 170 MPa
24700 psi
5mm/min; ISO 527
Elongation at Break 3.3 %
3.3 %
5mm/min; ISO 527
3.3 %
3.3 %
0.2 in/min; ASTM Test
3.9 %

@Temperature -40.0 °C
3.9 %

@Temperature -40.0 °F
ASTM Test
3.9 %

@Temperature -40.0 °C
3.9 %

@Temperature -40.0 °F
ISO Data
6.7 %

@Temperature 80.0 °C
6.7 %

@Temperature 176 °F
ASTM Test
6.7 %

@Temperature 80.0 °C
6.7 %

@Temperature 176 °F
ISO Data
7.0 %

@Temperature 120 °C
7.0 %

@Temperature 248 °F
ASTM Test
7.0 %

@Temperature 120 °C
7.0 %

@Temperature 248 °F
ISO Data
Flexural Strength 260 MPa
37700 psi
ASTM Test
Flexural Modulus 8.40 GPa
1220 ksi
ISO Data
8.97 GPa
1300 ksi
ASTM Test
Izod Impact, Notched 2.25 J/cm

@Thickness 3.17 mm
4.22 ft-lb/in

@Thickness 0.125 in
ASTM Test
Izod Impact, Notched (ISO) 26.0 kJ/m²
12.4 ft-lb/in²
ISO Test
18.0 kJ/m²

@Temperature -40.0 °C
8.57 ft-lb/in²

@Temperature -40.0 °F
ISO Test
Charpy Impact, Notched 2.30 J/cm²
10.9 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
10 K/min
220 °C
428 °F
ASTM Test
Deflection Temperature at 1.8 MPa (264 psi) 203 °C
397 °F
ISO 75
212 °C
414 °F
ASTM Test
Descriptive Properties Value Comments
Color Natural
Commercial Status Active America
Impact Modified Yes
Primary Processing Technique Injection Molding