BASF Ultramid® SEG7 35% Glass Filled PA6 (Dry)

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled
Manufacturer	BASF
Trade Name	Ultramid®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultramid® SEG7 35% Glass Filled PA6 (Dry).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Ultramid SEG7 is a 35% glass reinforced, injection molding type 6 nylon requiring high strength, surface aesthetics, and good processability. This product has excellent surface appearance while maintaining a good balance of physical properties, such as high strength, improved toughness, and chemical resistance. It features superior flow properties, and is suited for parts having thinner walls and those requiring long lengths. It shows lower pressure, temperature, and cycle time requirements than conventional grades.

Physical Properties	Metric	English	Comments
Density	1.41 g/cc	0.0509 lb/in³	ISO 1183
Water Absorption	1.0 %	1.0 %	24 hour; ISO Test
	6.3 %	6.3 %	ISO 62
Moisture Absorption at Equilibrium	1.7 %	1.7 %	23°C/50% R.H.; ISO 62
Linear Mold Shrinkage	0.0030 cm/cm	0.0030 in/in	ASTM Data; MD

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	120	120	ASTM Test
Tensile Strength at Break	185 MPa	26800 psi	0.2 in/min; ASTM Test
Tensile Strength, Ultimate	185 MPa	26800 psi	5mm/min; ISO 527
Elongation at Break	3.5 %	3.5 %	5mm/min; ISO 527
	3.5 %	3.5 %	0.2 in/min; ASTM Test
Flexural Strength	290 MPa	42100 psi	ASTM Test
Flexural Modulus	9.67 GPa	1400 ksi	ASTM Test
Izod Impact, Notched	1.50 J/cm @Thickness 3.17 mm	2.81 ft-lb/in @Thickness 0.125 in	ASTM Test

Thermal Properties	Metric	English	Comments
Melting Point	220 °C	428 °F	10 K/min
	220 °C	428 °F	ASTM Test
Flammability, UL94	HB @Thickness 0.710 mm	HB @Thickness 0.0280 in

Descriptive Properties	Value	Comments
Color	Natural
Commercial Status	Active America
Impact Modified	No
Primary Processing Technique	Injection Molding
Processing	Injection Molding
UL.UL-C	Yes