BASF Ultramid® HMG14 HS BK 102 60% Glass Filled PA66 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 60% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® HMG14 HS BK 102 60% Glass Filled PA66 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Ultramid HMG14 HS BK-102 is a 60% glass reinforced, injection molding grade of PA66 offering high strength and stiffness. Due to inherently lower moisture absorption, Ultramid HMG14 HS BK-102 shows improved retention of mechanical properties after moisture conditioning. In addition, molded parts possess an exceptional surface finish.Applications: Ultramid HMG14 HS BK-102 was designed for applications requiring very high rigidity and should be considered for components that are constructed with metal.Information provided by BASF
Physical Properties Metric English Comments
Density 1.75 g/cc
0.0632 lb/in³
ISO 1183
Mechanical Properties Metric English Comments
Tensile Strength at Break 248 MPa
36000 psi
ISO 527
Elongation at Break 2.2 %
2.2 %
ISO 527
Tensile Modulus 20.2 GPa
2930 ksi
ISO 527
Flexural Strength 383 MPa
55500 psi
ISO 178
Flexural Modulus 18.9 GPa
2740 ksi
ISO 178
Izod Impact, Notched (ISO) 12.0 kJ/m²
5.71 ft-lb/in²
ISO 180
13.0 kJ/m²
6.19 ft-lb/in²
ISO 180
Charpy Impact Unnotched 9.50 J/cm²

@Temperature -30.0 °C
45.2 ft-lb/in²

@Temperature -22.0 °F
ISO 179
9.90 J/cm²

@Temperature 23.0 °C
47.1 ft-lb/in²

@Temperature 73.4 °F
ISO 179
Charpy Impact, Notched 1.20 J/cm²

@Temperature -30.0 °C
5.71 ft-lb/in²

@Temperature -22.0 °F
ISO 179
1.30 J/cm²

@Temperature 23.0 °C
6.19 ft-lb/in²

@Temperature 73.4 °F
ISO 179
Thermal Properties Metric English Comments
Melting Point 260 °C
500 °F
ISO 3146
Deflection Temperature at 1.8 MPa (264 psi) 224 °C
435 °F
ISO 75
Processing Properties Metric English Comments
Melt Temperature 280 - 305 °C
536 - 581 °F
Mold Temperature 80.0 - 90.0 °C
176 - 194 °F
Dry Time 2 - 4 hour
2 - 4 hour
Moisture Content <= 0.12 %
<= 0.12 %
Descriptive Properties Value Comments
Color BK 102
Commercial Status North America