BASF Ultramid® FRee B3U31G4 20% Glass Filled PA66 FR (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® FRee B3U31G4 20% Glass Filled PA66 FR (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Halogen-free and phosphorus free flame retardant injection-molding grade with outstanding free-flow properties, good electrical properties and low smoke density; resistant to glow wire test up to 960°C.Information provided by BASF
Physical Properties Metric English Comments
Density 1.31 g/cc
0.0473 lb/in³
ISO 1183
Water Absorption 6.6 - 7.2 %
6.6 - 7.2 %
Saturation; ISO 62
Moisture Absorption at Equilibrium 2.0 - 2.4 %
2.0 - 2.4 %
23°C; 50% RH; ISO 62
Melt Flow 131 g/10 min

@Load 5.00 kg,
Temperature 275 °C
131 g/10 min

@Load 11.0 lb,
Temperature 527 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 40.0 MPa
5800 psi
50 mm/min; ISO 527-1/-2
Elongation at Yield 6.0 %
6.0 %
50 mm/min; ISO 527-1/-2
Modulus of Elasticity 2.90 GPa
421 ksi
ISO 527-1/-2
Flexural Modulus 2.80 GPa
406 ksi
ISO 178
Izod Impact, Notched (ISO) 6.00 kJ/m²

@Temperature 23.0 °C
2.86 ft-lb/in²

@Temperature 73.4 °F
ISO 180/A
Charpy Impact Unnotched 5.00 J/cm²

@Temperature 23.0 °C
23.8 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.600 J/cm²

@Temperature 23.0 °C
2.86 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow >= 90.0 µm/m-°C
>= 50.0 µin/in-°F
Melting Point 220 °C
428 °F
DIN 53765
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+11 ohm-cm
1.00e+11 ohm-cm
IEC 60093
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
IEC 60093
Comparative Tracking Index 525 V
525 V
Test solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 250 - 275 °C
482 - 527 °F
Injection-molding/Extrusion
Mold Temperature 80.0 - 90.0 °C
176 - 194 °F
Injection-molding
Descriptive Properties Value Comments
Commercial Status Europe