BASF Ultramid® C3UG4 20% Glass Filled PA6/66 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, 20% Glass Fiber Reinforced
Manufacturer BASF
Trade Name Ultramid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® C3UG4 20% Glass Filled PA6/66 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Halogen-free and phosphorus-free flame retardant injection-molding grade with outstanding free-flow properties, good electrical properties and low smoke density; resistant to glow wire test up to 960°C.Information provided by BASF
Physical Properties Metric English Comments
Density 1.31 g/cc
0.0473 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 2.0 - 2.4 %
2.0 - 2.4 %
23°C; 50% RH; ISO 62
Viscosity Measurement 130
130
ISO 307
Melt Flow 157.2 g/10 min

@Load 5.00 kg,
Temperature 275 °C
157.2 g/10 min

@Load 11.0 lb,
Temperature 527 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 95.0 MPa
13800 psi
50 mm/min; ISO 527-1/-2
Elongation at Yield 3.0 %
3.0 %
50 mm/min; ISO 527-1/-2
Modulus of Elasticity 6.00 GPa
870 ksi
ISO 527-1/-2
Charpy Impact Unnotched 3.50 J/cm²

@Temperature 23.0 °C
16.7 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Thermal Properties Metric English Comments
Melting Point 240 °C
464 °F
DIN 53765
Deflection Temperature at 0.46 MPa (66 psi) 210 °C
410 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 195 °C
383 °F
ISO 75-1/-2
Flammability, UL94 V-2

@Thickness >=0.800 mm
V-2

@Thickness >=0.0315 in
Electrical Properties Metric English Comments
Comparative Tracking Index 550 V
550 V
Test solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 250 - 270 °C
482 - 518 °F
Injection-molding/Extrusion
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Injection-molding
Descriptive Properties Value Comments
Commercial Status Europe