BASF Ultramid® C3U PA66/6 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, Unreinforced
Manufacturer BASF
Trade Name Ultramid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® C3U PA66/6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid C3U is an injection molding, general purpose PA66/6 grade with improved flame retardance.
Physical Properties Metric English Comments
Density 1.16 g/cc
0.0419 lb/in³
ISO 1183
Water Absorption 8.0 - 9.0 %
8.0 - 9.0 %
ISO 62
Moisture Absorption at Equilibrium 2.6 - 3.2 %
2.6 - 3.2 %
23°C/50% R.H.; ISO 62
Viscosity Test 150 cm³/g
150 cm³/g
Viscosity number; ISO 307
Linear Mold Shrinkage 0.0080 cm/cm
0.0080 in/in
Melt Flow 162 g/10 min

@Load 5.00 kg,
Temperature 275 °C
162 g/10 min

@Load 11.0 lb,
Temperature 527 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 75.0 MPa
10900 psi
50mm/min; ISO 527
Elongation at Yield 4.0 %
4.0 %
50mm/min; ISO 527
Modulus of Elasticity 3.50 GPa
508 ksi
ISO 527
Flexural Modulus 3.00 GPa
435 ksi
ISO 178
Izod Impact, Notched (ISO) 4.50 kJ/m²
2.14 ft-lb/in²
ISO 180/A
3.50 kJ/m²

@Temperature -30.0 °C
1.67 ft-lb/in²

@Temperature -22.0 °F
ISO 180/A
Charpy Impact Unnotched 8.00 J/cm²
38.1 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 0.600 J/cm²
2.86 ft-lb/in²
ISO 179/1eA
0.400 J/cm²

@Temperature -30.0 °C
1.90 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 60.0 - 100 µm/m-°C

@Temperature 23.0 - 80.0 °C
33.3 - 55.6 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 60.0 - 120 µm/m-°C

@Temperature 23.0 - 80.0 °C
33.3 - 66.7 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-1/-2
Specific Heat Capacity 1.70 J/g-°C
0.406 BTU/lb-°F
Thermal Conductivity 0.330 W/m-K
2.29 BTU-in/hr-ft²-°F
DIN 52612
Melting Point 243 °C
469 °F
DIN 53765
Maximum Service Temperature, Air 107 °C
225 °F
for 50% loss of tensile strength after 20,000 hr
123 °C
253 °F
for 50% loss of tensile strength after 5,000 hr
200 °C
392 °F
Deflection Temperature at 0.46 MPa (66 psi) 210 °C
410 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 70.0 °C
158 °F
ISO 75
Flammability, UL94 V-0

@Thickness >=0.400 mm
V-0

@Thickness >=0.0157 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
IEC 60093
Dielectric Constant 3.6

@Frequency 1.00e+6 Hz
3.6

@Frequency 1.00e+6 Hz
IEC 60250
Dissipation Factor 0.020

@Frequency 1.00e+6 Hz
0.020

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
Test Solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 250 - 270 °C
482 - 518 °F
Injection-molding/Extrusion
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Injection-molding
Descriptive Properties Value Comments
Color Natural
Commercial Status North America and Europe
Impact Modified No
Primary Processing Technique Injection Molding