BASF Ultramid® BG40GM45 HS BK 00130 20/25 % Glass/Mineral Filled PA6 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass/Mineral Reinforced
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® BG40GM45 HS BK 00130 20/25 % Glass/Mineral Filled PA6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Ultramid® BG40GM45 HS BK-130 is a pigmented black, heat stabilized, 45 % glass and mineral fiber reinforced polyamide 6 injection molding compound. It possesses a balance of engineering properties in combination with excellent dimensional stability, low warp and resistance to sink-mark-formation. It is ideally suited for applications such as rotors, wheels, rims, timing belt covers, automotive cooling fans, shrouds as well as interior and exterior door handles.Information provided by BASF
Physical Properties Metric English Comments
Bulk Density 0.500 - 0.800 g/cc
0.0181 - 0.0289 lb/in³
Density 1.51 g/cc
0.0546 lb/in³
ISO 1183
Viscosity Measurement 142
142
ISO 307
Mechanical Properties Metric English Comments
Ball Indentation Hardness 250 MPa

@Load 3.06 kg
36300 psi

@Load 6.74 lb
358; ISO 2039-2
Tensile Strength, Yield 140 MPa
20300 psi
ISO 527-2
Elongation at Break 2.0 %
2.0 %
ISO 527-2
Tensile Modulus 10.5 GPa
1520 ksi
ISO 527-2
Flexural Strength 210 MPa
30500 psi
ISO 178
Flexural Modulus 8.70 GPa
1260 ksi
ISO 178
Charpy Impact Unnotched 5.00 J/cm²

@Temperature 23.0 °C
23.8 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.600 J/cm²

@Temperature 23.0 °C
2.86 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
ISO 3146
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi) 200 °C
392 °F
ISO 75-2
Decomposition Temperature >= 300 °C
>= 572 °F
Processing Properties Metric English Comments
Processing Temperature 80.0 °C
176 °F
Hopper Throat
Zone 1 270 °C
518 °F
Feed Zone
Zone 2 280 °C
536 °F
Compression
Zone 3 290 °C
554 °F
Metering-zone
Zone 4 290 °C
554 °F
Nozzle
Melt Temperature 280 - 300 °C
536 - 572 °F
Injection Molding/Extrusion
290 °C
554 °F
Optimal
Mold Temperature 80.0 °C
176 °F
Optimal
80.0 - 90.0 °C
176 - 194 °F
Injection Molding/Extrusion
Drying Temperature 80.0 °C
176 °F
Dry Time 4 hour
4 hour
Moisture Content 0.030 - 0.060 %
0.030 - 0.060 %
Optimal
<= 0.15 %
<= 0.15 %
Descriptive Properties Value Comments
Color BK 00130
Commercial Status Europe
Ignition Temperature >400°C
ASTM D1929
Peripheral screw speed < 0.3 m/s