BASF Ultramid® B3ZG8 BK 20560 40% Glass Filled PA6-1 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® B3ZG8 BK 20560 40% Glass Filled PA6-1 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Impact-modified and 40% glass-fiber reinforced injection-molding grade for technical articles of very high stiffness and toughness, for instance, for vehicle airbag housings and suitcase shell.Information provided by BASF
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
ISO 1183
Water Absorption 4.7 - 5.3 %
4.7 - 5.3 %
Saturation; ISO 62
Moisture Absorption at Equilibrium 1.4 - 1.8 %
1.4 - 1.8 %
23°C; 50% RH; ISO 62
Viscosity Measurement 160
160
ISO 307
Linear Mold Shrinkage 0.0035 cm/cm
0.0035 in/in
restricted
Melt Flow 12.6 g/10 min

@Load 5.00 kg,
Temperature 275 °C
12.6 g/10 min

@Load 11.0 lb,
Temperature 527 °F
ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 84.0 MPa

@Load 36.5 kg,
Time 30.0 sec
12200 psi

@Load 80.5 lb,
Time 0.00833 hour
ISO 2039-1
Tensile Strength, Yield 165 MPa
23900 psi
50 mm/min; ISO 527-1/-2
Elongation at Yield 4.6 %
4.6 %
50 mm/min; ISO 527-1/-2
Modulus of Elasticity 11.6 GPa
1680 ksi
ISO 527-1/-2
Flexural Strength 250 MPa
36300 psi
at max force; ISO 178
Flexural Modulus 9.50 GPa
1380 ksi
ISO 178
Izod Impact, Notched (ISO) 14.0 kJ/m²

@Temperature -30.0 °C
6.66 ft-lb/in²

@Temperature -22.0 °F
ISO 180/A
22.0 kJ/m²

@Temperature 23.0 °C
10.5 ft-lb/in²

@Temperature 73.4 °F
ISO 180/A
Charpy Impact Unnotched 10.5 J/cm²

@Temperature -30.0 °C
50.0 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
11.0 J/cm²

@Temperature 23.0 °C
52.3 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 1.50 J/cm²

@Temperature -30.0 °C
7.14 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
2.40 J/cm²

@Temperature 23.0 °C
11.4 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 10.0 - 20.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
5.56 - 11.1 µin/in-°F

@Temperature 73.4 - 176 °F
DIN 11359-1/-2
CTE, linear, Transverse to Flow 50.0 - 60.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
27.8 - 33.3 µin/in-°F

@Temperature 73.4 - 176 °F
DIN 11359-1/-2
Thermal Conductivity 0.360 W/m-K
2.50 BTU-in/hr-ft²-°F
DIN 52612
Melting Point 220 °C
428 °F
DIN 53765
Maximum Service Temperature, Air 180 °C
356 °F
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 205 °C
401 °F
ISO 75-1/-2
Decomposition Temperature >= 300 °C
>= 572 °F
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
IEC 60093
Surface Resistance 1.00e+12 ohm
1.00e+12 ohm
IEC 60093
Dielectric Constant 4.0

@Frequency 1.00 Hz
4.0

@Frequency 1.00 Hz
IEC 60250
Dissipation Factor 0.020

@Frequency 1.00e+6 Hz
0.020

@Frequency 1.00e+6 Hz
IEC 60250
Processing Properties Metric English Comments
Processing Temperature 80.0 °C
176 °F
Hopper Throat
Zone 1 260 °C
500 °F
Feed Zone
Zone 2 270 °C
518 °F
Compression
Zone 3 280 °C
536 °F
Metering-zone
Zone 4 280 °C
536 °F
Nozzle
Melt Temperature 270 - 290 °C
518 - 554 °F
Injection-molding/Extrusion
280 °C
536 °F
Optimal
Mold Temperature 80.0 °C
176 °F
Optimal
80.0 - 90.0 °C
176 - 194 °F
Injection-molding
Drying Temperature 80.0 °C
176 °F
Dry Time 4 hour
4 hour
Moisture Content 0.030 - 0.060 %
0.030 - 0.060 %
Optimal
<= 0.15 %
<= 0.15 %
Descriptive Properties Value Comments
Color BK 20560
Commercial Status Europe
Ignition Temperature >400°C
ASTM D129
Peripheral screw speed < 0.3 m/s
Copyright © lookpolymers.com All Rights Reserved