BASF Ultramid® B3WG6 30% Glass Filled PA6 (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® B3WG6 30% Glass Filled PA6 (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultramid B3WG6 is a 30% glass fiber reinforced, heat stabilized injection molding PA6 grade.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 |
| Water Absorption | 6.3 - 6.9 % | 6.3 - 6.9 % | ISO 62 |
| Moisture Absorption at Equilibrium | 1.9 - 2.3 % | 1.9 - 2.3 % | (23°C/50% R.H.); ISO 62 |
| Viscosity Test | 140 cm³/g | 140 cm³/g | Viscosity number; ISO 307 |
| Linear Mold Shrinkage | 0.0035 cm/cm | 0.0035 in/in | |
| Melt Flow | 68 g/10 min @Load 5.00 kg, Temperature 275 °C |
68 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 115 MPa | 16700 psi | 50mm/min; ISO 527 |
| Elongation at Yield | 8.0 % | 8.0 % | 50mm/min; ISO 527 |
| Flexural Strength | 180 MPa | 26100 psi | ISO 178 |
| Flexural Modulus | 5.00 GPa | 725 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 20.0 kJ/m² | 9.52 ft-lb/in² | ISO 180/A |
| Charpy Impact Unnotched | 11.0 J/cm² | 52.4 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 3.00 J/cm² | 14.3 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 1.50 J/g-°C | 0.359 BTU/lb-°F | |
| Thermal Conductivity | 0.360 W/m-K | 2.50 BTU-in/hr-ft²-°F | DIN 52612 |
| Melting Point | 220 °C | 428 °F | DIN 53765 |
| Maximum Service Temperature, Air | 145 °C | 293 °F | for 50% loss of tensile strength after 20,000 hr |
| 175 °C | 347 °F | for 50% loss of tensile strength after 5,000 hr | |
| 200 °C | 392 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 |
| Dielectric Constant | 6.8 @Frequency 1.00e+6 Hz |
6.8 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dissipation Factor | 0.22 @Frequency 1.00e+6 Hz |
0.22 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 450 V | 450 V | Test Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | Injection-molding/Extrusion |
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Injection-molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural | |
| Commercial Status | North America and Europe | |
| Form | Pellets | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding | |
| Processing | Injection Molding | |
| Special characteristic | Heat stabilized or stable to heat |
Users viewing this material also viewed the following:
- Idemitsu Kosan Xarec® WA 212 SPS, 30% Glass Filled
- LG Chemical Methyl Acrylate
- A. Schulman SCHULAMID® 66 GF13 13% Glass Fiber Reinforced Nylon 66
- Plenco 6401 Phenolic, Briquette, Transfer Molded
- ExxonMobil Enable™ 20-10CB Metallocene Polyethylene Resin
- Dow C702-20 Polypropylene Impact Copolymer Resin
- Dow CYCLOTENE™ 4022-35 Advanced Electronic Resins (PhotoBisbenzocyclobutene BCB)
- Arkema Group Orgalloy® LE 60XV Flexible Nylon Alloy (Conditioned)
Copyright © lookpolymers.com All Rights Reserved