BASF Ultramid® B3M6 BK 23213 30% Mineral Filled PA6 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Mineral Filled
Manufacturer BASF
Trade Name Ultramid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® B3M6 BK 23213 30% Mineral Filled PA6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: 30% Mineral-filled injection molding grade for high impact industrial items having very high dimensional stability, such as automobile wheel covers.Information provided by BASF
Physical Properties Metric English Comments
Bulk Density 0.500 - 0.800 g/cc
0.0181 - 0.0289 lb/in³
Density 1.36 g/cc
0.0491 lb/in³
ISO 1183
Water Absorption 5.9 - 6.5 %
5.9 - 6.5 %
ISO 62
Moisture Absorption at Equilibrium 2.2 - 2.6 %
2.2 - 2.6 %
ISO 62
Viscosity Measurement 145
145
ISO 307
Linear Mold Shrinkage 0.0075 cm/cm
0.0075 in/in
Melt Flow 81.6 g/10 min

@Load 5.00 kg,
Temperature 275 °C
81.6 g/10 min

@Load 11.0 lb,
Temperature 527 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 75.0 MPa
10900 psi
ISO 527-1/-2
Elongation at Break 12 %
12 %
ISO 527-1/-2
Tensile Modulus 4.60 GPa
667 ksi
ISO 527-1/-2
Flexural Strength 125 MPa
18100 psi
ISO 178
Flexural Modulus 4.00 GPa
580 ksi
ISO 178
Izod Impact, Notched (ISO) 6.50 kJ/m²

@Temperature 23.0 °C
3.09 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1A
Charpy Impact Unnotched 10.0 J/cm²

@Temperature -30.0 °C
47.6 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
19.0 J/cm²

@Temperature 23.0 °C
90.4 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.500 J/cm²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
0.900 J/cm²

@Temperature 23.0 °C
4.28 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 50.0 - 80.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
27.8 - 44.4 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 50.0 - 70.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
27.8 - 38.9 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-1/-2
Thermal Conductivity 0.310 W/m-K
2.15 BTU-in/hr-ft²-°F
DIN 52612-1
Melting Point 220 °C
428 °F
ISO 11357-1/-3
Maximum Service Temperature, Air 100 °C
212 °F
for 50% loss of tensile strength after 20000hr
180 °C
356 °F
Deflection Temperature at 0.46 MPa (66 psi) 195 °C
383 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 70.0 °C
158 °F
ISO 75-1/-2
Decomposition Temperature >= 300 °C
>= 572 °F
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
IEC 60093
Dielectric Constant 3.5

@Frequency 1.00e+6 Hz
3.5

@Frequency 1.00e+6 Hz
IEC 60250
Dissipation Factor 0.020

@Frequency 1.00e+6 Hz
0.020

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 450 V
450 V
Test Solution A; IEC 60112
Processing Properties Metric English Comments
Processing Temperature 80.0 °C
176 °F
Hopper Throat
Zone 1 260 °C
500 °F
Feed Zone
Zone 2 370 °C
698 °F
Compression
Zone 3 280 °C
536 °F
Metering-zone
Zone 4 280 °C
536 °F
Nozzle
Melt Temperature 270 - 290 °C
518 - 554 °F
Injection Molding/Extrusion
280 °C
536 °F
Optimal
Mold Temperature 80.0 °C
176 °F
Optimal
80.0 - 90.0 °C
176 - 194 °F
Injection Molding
Drying Temperature 80.0 °C
176 °F
Dry Time 4 hour
4 hour
Descriptive Properties Value Comments
Color BK 23213
Commercial Status Europe
Ignition Temperature >400°C
ASTM D1929
Peripheral screw speed < 0.3 m/s