BASF Ultramid® B3K BK00464 PA6 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced
Manufacturer BASF
Trade Name Ultramid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® B3K BK00464 PA6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Easy flowing and stabilized injection-molding grade used for technical parts with wall thicknesses >2 mm, e.g. machinery components, fans and power tool housings.Information provided by BASF
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
ISO 1183
Water Absorption 9.0 - 10 %
9.0 - 10 %
Saturation; ISO 62
Moisture Absorption at Equilibrium 2.6 - 3.4 %
2.6 - 3.4 %
23°C; 50% RH; ISO 62
Viscosity Measurement 150
150
ISO 307
Linear Mold Shrinkage 0.0065 cm/cm
0.0065 in/in
restricted
Melt Flow 180.8 g/10 min

@Load 5.00 kg,
Temperature 275 °C
180.8 g/10 min

@Load 11.0 lb,
Temperature 527 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 85.0 MPa
12300 psi
50 mm/min; ISO 527-1/-2
Elongation at Yield 4.5 %
4.5 %
50 mm/min; ISO 527-1/-2
Modulus of Elasticity 3.00 GPa
435 ksi
ISO 527-1/-2
Flexural Modulus 2.80 GPa
406 ksi
ISO 178
Izod Impact, Notched (ISO) 5.00 kJ/m²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
ISO 180/A
5.50 kJ/m²

@Temperature 23.0 °C
2.62 ft-lb/in²

@Temperature 73.4 °F
ISO 180/A
Charpy Impact Unnotched 10.0 J/cm²

@Temperature -30.0 °C
47.6 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.400 J/cm²

@Temperature -30.0 °C
1.90 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
0.550 J/cm²

@Temperature 23.0 °C
2.62 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 70.0 - 100 µm/m-°C

@Temperature 23.0 - 80.0 °C
38.9 - 55.6 µin/in-°F

@Temperature 73.4 - 176 °F
DIN 11359-1/-2
Specific Heat Capacity 1.70 J/g-°C
0.406 BTU/lb-°F
Thermal Conductivity 0.330 W/m-K
2.29 BTU-in/hr-ft²-°F
DIN 52612
Melting Point 220 °C
428 °F
DIN 53765
Maximum Service Temperature, Air 100 °C
212 °F
for 50% loss of tensile strength after 20000hr
112 °C
234 °F
for 50% loss of tensile strength after 5000hr
180 °C
356 °F
Deflection Temperature at 0.46 MPa (66 psi) 180 °C
356 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 65.0 °C
149 °F
ISO 75-1/-2
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
IEC 60093
Dielectric Constant 3.5

@Frequency 1.00 Hz
3.5

@Frequency 1.00 Hz
IEC 60250
Dissipation Factor 0.032

@Frequency 1.00e+6 Hz
0.032

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
Test solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 250 - 270 °C
482 - 518 °F
Injection-molding/Extrusion
Mold Temperature 40.0 - 80.0 °C
104 - 176 °F
Injection-molding
Descriptive Properties Value Comments
Commercial Status Europe