BASF Ultramid® B35EG3 BK 00564 15% Glass Filled PA6 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® B35EG3 BK 00564 15% Glass Filled PA6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: 15% glass-fiber reinforced injection-molding grade for gIT applications such as, for example, steering column switches, vehicle mirror housings and the wheels of mountain bikes.Information provided by BASF
Physical Properties Metric English Comments
Bulk Density 0.500 - 0.800 g/cc
0.0181 - 0.0289 lb/in³
Density 1.23 g/cc
0.0444 lb/in³
ISO 1183
Water Absorption 7.7 - 8.3 %
7.7 - 8.3 %
Saturation; ISO 62
Moisture Absorption at Equilibrium 2.3 - 2.9 %
2.3 - 2.9 %
23°C; 50% RH; ISO 62
Viscosity Measurement 170
170
ISO 307
Linear Mold Shrinkage 0.0055 cm/cm
0.0055 in/in
restricted
Melt Flow 67.65 g/10 min

@Load 5.00 kg,
Temperature 275 °C
67.65 g/10 min

@Load 11.0 lb,
Temperature 527 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 130 MPa
18900 psi
50 mm/min; ISO 527-1/-2
Elongation at Yield 4.0 %
4.0 %
50 mm/min; ISO 527-1/-2
Modulus of Elasticity 5.80 GPa
841 ksi
ISO 527-1/-2
Flexural Strength 180 MPa
26100 psi
at max force; ISO 178
Flexural Modulus 5.20 GPa
754 ksi
ISO 178
Izod Impact, Notched (ISO) 6.50 kJ/m²

@Temperature 23.0 °C
3.09 ft-lb/in²

@Temperature 73.4 °F
ISO 180/A
Charpy Impact Unnotched 5.50 J/cm²

@Temperature -30.0 °C
26.2 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
6.00 J/cm²

@Temperature 23.0 °C
28.6 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.800 J/cm²

@Temperature -30.0 °C
3.81 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
0.900 J/cm²

@Temperature 23.0 °C
4.28 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 30.0 - 35.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
16.7 - 19.4 µin/in-°F

@Temperature 73.4 - 176 °F
DIN 11359-1/-2
CTE, linear, Transverse to Flow 70.0 - 80.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
38.9 - 44.4 µin/in-°F

@Temperature 73.4 - 176 °F
DIN 11359-1/-2
Thermal Conductivity 0.340 W/m-K
2.36 BTU-in/hr-ft²-°F
DIN 52612
Melting Point 220 °C
428 °F
DIN 53765
Maximum Service Temperature, Air 135 °C
275 °F
for 50% loss of tensile strength after 20000hr
165 °C
329 °F
for 50% loss of tensile strength after 5000hr
200 °C
392 °F
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 190 °C
374 °F
ISO 75-1/-2
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
IEC 60093
Dielectric Constant 3.8

@Frequency 1.00 Hz
3.8

@Frequency 1.00 Hz
IEC 60250
Dissipation Factor 0.025

@Frequency 1.00e+6 Hz
0.025

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 550 V
550 V
Test solution A; IEC 60112
Processing Properties Metric English Comments
Processing Temperature 80.0 °C
176 °F
Hopper Throat
Zone 1 260 °C
500 °F
Feed Zone
Zone 2 270 °C
518 °F
Compression
Zone 3 280 °C
536 °F
Metering-zone
Zone 4 280 °C
536 °F
Nozzle
Melt Temperature 270 - 290 °C
518 - 554 °F
Injection-molding/Extrusion
290 °C
554 °F
Optimal
Mold Temperature 80.0 °C
176 °F
Optimal
80.0 - 90.0 °C
176 - 194 °F
Injection-molding
Drying Temperature 80.0 °C
176 °F
Dry Time 4 hour
4 hour
Descriptive Properties Value Comments
Color BK 00564
Commercial Status Europe
Peripheral screw speed < 0.3 m/s