BASF Ultramid® B27 E 01 PA6 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® B27 E 01 PA6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid B27 E 01 is a low viscosity general-purpose, extrusion PA6 grade well suited for compounding. It conforms to FDA requirements including, 21 CFR 177.1500,EU Directive 2002/72/EC, the German BfR recommendation "X Polyamide", 1.6.1998 or legislations for other countries will be provided on request.
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
ISO 1183
Water Absorption 9.5 %
9.5 %
ISO 62
Moisture Absorption at Equilibrium 2.6 %
2.6 %
23°C/50% R.H.; ISO 62
Relative Viscosity 2.7 cP
2.7 cP
ISO Test; 96 % SAV
Viscosity Test 150 cm³/g
150 cm³/g
Viscosity number
Linear Mold Shrinkage 0.010 cm/cm
0.010 in/in
ASTM Data; MD
Melt Flow 130 g/10 min

@Load 5.00 kg,
Temperature 275 °C
130 g/10 min

@Load 11.0 lb,
Temperature 527 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 80.0 MPa
11600 psi
2 in/min; ASTM Test
90.0 MPa
13100 psi
50mm/min; ISO 527
Elongation at Break 15 %
15 %
50mm/min, Nominal strain; ISO 527
Elongation at Yield 4.5 %
4.5 %
50mm/min; ISO 527
Tensile Modulus 3.00 GPa
435 ksi
1mm/min; ISO 527
3.00 GPa
435 ksi
ASTM Test
Izod Impact, Notched 0.480 J/cm

@Temperature -40.0 °C
0.899 ft-lb/in

@Temperature -40.0 °F
ASTM Test
0.530 J/cm

@Thickness 3.17 mm
0.993 ft-lb/in

@Thickness 0.125 in
ASTM Test
Charpy Impact Unnotched NB
NB
ISO 179
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
ISO 179
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179
Thermal Properties Metric English Comments
CTE, linear 40.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
22.2 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM Test
CTE, linear, Parallel to Flow 85.0 µm/m-°C
47.2 µin/in-°F
ISO 11359
Melting Point 220 °C
428 °F
10 K/min
220 °C
428 °F
ASTM Test
Deflection Temperature at 0.46 MPa (66 psi) 160 °C
320 °F
ASTM Test
160 °C
320 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 54.0 °C
129 °F
ASTM Test
65.0 °C
149 °F
ISO 75
Vicat Softening Point 204 °C
399 °F
(50 °C/h / 50N) - B/50; ISO 306
Glass Transition Temp, Tg 60.0 °C
140 °F
10 K/min; ISO 11357-1/-3
Oxygen Index 26 %
26 %
ISO 4589-1/-2
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
IEC 60093
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
IEC 60093
Dielectric Constant 3.5

@Frequency 1.00e+6 Hz
3.5

@Frequency 1.00e+6 Hz
IEC 60250
4.0

@Frequency 100 Hz
4.0

@Frequency 100 Hz
IEC 60250
Dissipation Factor 0.010

@Frequency 100 Hz
0.010

@Frequency 100 Hz
IEC 60250
0.023

@Frequency 1.00e+6 Hz
0.023

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
IEC 60112
Descriptive Properties Value Comments
Color Natural
Commercial Status North America and Europe
FDA 21 CFR 177.1500
Form Pellets
Impact Modified No
Primary Processing Technique Injection Molding
Processing Other Extrusion