BASF Ultramid® A3WG3 15% Glass Filled PA66 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® A3WG3 15% Glass Filled PA66 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: 15% Glass-fiber reinforced and heat aging resistant injection-molding grade for machine elements and housings of medium stiffness. For electric insulating parts, preference should be given to the grades A3Eg3 and A3hg3Information provided by BASF
Physical Properties Metric English Comments
Density 1.23 g/cc
0.0444 lb/in³
ISO 1183
Water Absorption 6.7 - 7.3 %
6.7 - 7.3 %
Saturation; ISO 62
Moisture Absorption at Equilibrium 1.9 - 2.5 %
1.9 - 2.5 %
23°C; 50% RH; ISO 62
Viscosity Measurement 145
145
ISO 307
Linear Mold Shrinkage 0.0075 cm/cm
0.0075 in/in
restricted
Melt Flow 73.8 g/10 min

@Load 5.00 kg,
Temperature 275 °C
73.8 g/10 min

@Load 11.0 lb,
Temperature 527 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 130 MPa
18900 psi
50 mm/min; ISO 527-1/-2
Elongation at Yield 3.0 %
3.0 %
50 mm/min; ISO 527-1/-2
Modulus of Elasticity 6.00 GPa
870 ksi
ISO 527-1/-2
Flexural Strength 200 MPa
29000 psi
at max force; ISO 178
Flexural Modulus 5.50 GPa
798 ksi
ISO 178
Izod Impact, Notched (ISO) 5.50 kJ/m²

@Temperature 23.0 °C
2.62 ft-lb/in²

@Temperature 73.4 °F
ISO 180/A
Charpy Impact Unnotched 4.30 J/cm²

@Temperature -30.0 °C
20.5 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
4.50 J/cm²

@Temperature 23.0 °C
21.4 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.700 J/cm²

@Temperature -30.0 °C
3.33 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
0.800 J/cm²

@Temperature 23.0 °C
3.81 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 30.0 - 35.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
16.7 - 19.4 µin/in-°F

@Temperature 73.4 - 176 °F
DIN 11359-1/-2
CTE, linear, Transverse to Flow 70.0 - 80.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
38.9 - 44.4 µin/in-°F

@Temperature 73.4 - 176 °F
DIN 11359-1/-2
Specific Heat Capacity 1.80 J/g-°C
0.430 BTU/lb-°F
Thermal Conductivity 0.330 W/m-K
2.29 BTU-in/hr-ft²-°F
DIN 52612
Melting Point 260 °C
500 °F
DIN 53765
Maximum Service Temperature, Air 145 °C
293 °F
for 50% loss of tensile strength after 20000hr
175 °C
347 °F
for 50% loss of tensile strength after 5000hr
240 °C
464 °F
Deflection Temperature at 0.46 MPa (66 psi) 250 °C
482 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 240 °C
464 °F
ISO 75-1/-2
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
IEC 60093
Dielectric Constant 3.5

@Frequency 1.00 Hz
3.5

@Frequency 1.00 Hz
IEC 60250
Dissipation Factor 0.0014

@Frequency 1.00e+6 Hz
0.0014

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 450 V
450 V
Test solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 280 - 300 °C
536 - 572 °F
Injection-molding/Extrusion
Mold Temperature 80.0 - 90.0 °C
176 - 194 °F
Injection-molding
Descriptive Properties Value Comments
Commercial Status Europe