BASF Ultramid® A3HG6 Balance 30% Glass Filled PA 66/610 (Conditioned)

Category	Polymer , Thermoplastic , Nylon , Nylon 610 , Nylon 610, Glass Reinforced
Manufacturer	BASF
Trade Name	Ultramid®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultramid® A3HG6 Balance 30% Glass Filled PA 66/610 (Conditioned).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: BASF supplies polyamide 610 for processing by injection molding under the trade name Ultramid® Balance which is produced by polycondensation of hexamethylene diamine and sebacic acid. This means that more than 60 % of the base polymer for the product family consists of sustainable raw materials. Ultramid® S Balance is highly resistant to fuels, oils and greases, to most solvents, aqueous solutions and alkalis. Its resistance to weakly acid media makes it superior to PA 6 and PA 66. Applications: Oil pans and oil filter housingsRadiator end caps Components in contact with aggressive spray waterInformation provided by BASF

Physical Properties	Metric	English	Comments
Density	1.343 g/cc	0.04852 lb/in³	ISO 1183
Water Absorption	3.8 %	3.8 %	ISO 62
Moisture Absorption at Equilibrium	1.3 %	1.3 %	ISO 62
Viscosity Measurement	150	150	[cm<sup>3</sup>/g]; ISO 307
Linear Mold Shrinkage, Flow	0.0040 cm/cm	0.0040 in/in	ISO 2577
Linear Mold Shrinkage, Transverse	0.010 cm/cm	0.010 in/in	ISO 2577
Melt Flow	26.86 g/10 min @Load 5.00 kg, Temperature 275 °C	26.86 g/10 min @Load 11.0 lb, Temperature 527 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	125 MPa	18100 psi	ISO 527-1/-2
Elongation at Yield	5.0 %	5.0 %	ISO 527-1/-2
Modulus of Elasticity	7.20 GPa	1040 ksi	ISO 527-1/-2
Flexural Strength	200 MPa	29000 psi	ISO 178
Flexural Modulus	6.70 GPa	972 ksi	ISO 178
Charpy Impact Unnotched	9.00 J/cm² @Temperature 23.0 °C	42.8 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eU
Charpy Impact, Notched	1.40 J/cm² @Temperature 23.0 °C	6.66 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Melting Point	260 °C	500 °F	ISO 11357-1/-3

Processing Properties	Metric	English	Comments
Melt Temperature	270 - 290 °C	518 - 554 °F	Injection molding
Mold Temperature	80.0 - 90.0 °C	176 - 194 °F	Injection molding/Extrusion

Descriptive Properties	Value	Comments
Commercial Status	Europe