BASF Ultramid® A3EG10 50% Glass Filled PA66 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 50% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® A3EG10 50% Glass Filled PA66 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: 50% glass-fiber reinforced injection-molding grade for technical articles of very high stiffness as well as for electric insulating parts.Information provided by BASF
Physical Properties Metric English Comments
Bulk Density 0.500 - 0.800 g/cc
0.0181 - 0.0289 lb/in³
Density 1.56 g/cc
0.0564 lb/in³
ISO 1183
Water Absorption 3.7 - 4.3 %
3.7 - 4.3 %
Saturation; ISO 62
Moisture Absorption at Equilibrium 1.0 - 1.4 %
1.0 - 1.4 %
23°C; 50% RH; ISO 62
Viscosity Measurement 130
130
ISO 307
Linear Mold Shrinkage 0.0045 cm/cm
0.0045 in/in
restricted
Linear Mold Shrinkage, Flow 0.0033 cm/cm
0.0033 in/in
ISO 2577
0.0045 cm/cm
0.0045 in/in
TM=300°C, TW=80°C
Linear Mold Shrinkage, Transverse 0.0082 cm/cm
0.0082 in/in
ISO 2577
Melt Flow 31.2 g/10 min

@Load 5.00 kg,
Temperature 275 °C
31.2 g/10 min

@Load 11.0 lb,
Temperature 527 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 240 MPa
34800 psi
50 mm/min; ISO 527-1/-2
Elongation at Yield 2.5 %
2.5 %
50 mm/min; ISO 527-1/-2
Modulus of Elasticity 16.8 GPa
2440 ksi
ISO 527-1/-2
Flexural Strength 360 MPa
52200 psi
at max force; ISO 178
Flexural Modulus 15.0 GPa
2180 ksi
ISO 178
Izod Impact, Notched (ISO) 13.0 kJ/m²

@Temperature 23.0 °C
6.19 ft-lb/in²

@Temperature 73.4 °F
ISO 180/A
Charpy Impact Unnotched 9.00 J/cm²

@Temperature -30.0 °C
42.8 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
9.50 J/cm²

@Temperature 23.0 °C
45.2 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 1.30 J/cm²

@Temperature -30.0 °C
6.19 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
1.80 J/cm²

@Temperature 23.0 °C
8.57 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 5.00 - 20.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
2.78 - 11.1 µin/in-°F

@Temperature 73.4 - 176 °F
DIN 11359-1/-2
CTE, linear, Transverse to Flow 50.0 - 60.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
27.8 - 33.3 µin/in-°F

@Temperature 73.4 - 176 °F
DIN 11359-1/-2
Specific Heat Capacity 1.30 J/g-°C
0.311 BTU/lb-°F
Thermal Conductivity 0.370 W/m-K
2.57 BTU-in/hr-ft²-°F
DIN 52612
Melting Point 260 °C
500 °F
DIN 53765
Maximum Service Temperature, Air 135 °C
275 °F
for 50% loss of tensile strength after 20000hr
165 °C
329 °F
for 50% loss of tensile strength after 5000hr
240 °C
464 °F
Deflection Temperature at 0.46 MPa (66 psi) 250 °C
482 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 250 °C
482 °F
ISO 75-1/-2
Decomposition Temperature >= 310 °C
>= 590 °F
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
IEC 60093
Dielectric Constant 3.8

@Frequency 1.00 Hz
3.8

@Frequency 1.00 Hz
IEC 60250
Dissipation Factor 0.015

@Frequency 1.00e+6 Hz
0.015

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 550 V
550 V
Test solution A; IEC 60112
Processing Properties Metric English Comments
Processing Temperature 80.0 °C
176 °F
Hopper Throat
Zone 1 300 °C
572 °F
Feed zone
Zone 2 300 °C
572 °F
Compression
Zone 3 300 °C
572 °F
Metering-zone
Zone 4 300 °C
572 °F
Nozzle
Melt Temperature 290 - 310 °C
554 - 590 °F
Injection-molding/Extrusion
300 °C
572 °F
Optimal
Mold Temperature 80.0 °C
176 °F
Optimal
80.0 - 90.0 °C
176 - 194 °F
Injection-molding
Drying Temperature 80.0 °C
176 °F
Dry Time 4 hour
4 hour
Moisture Content 0.030 - 0.060 %
0.030 - 0.060 %
Optimal
<= 0.15 %
<= 0.15 %
Descriptive Properties Value Comments
Commercial Status Europe
Ignition Temperature >400°C
ASTM D129
Peripheral screw speed < 0.3 m/s