BASF Ultramid® 8351 HS BK 102 PA6 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® 8351 HS BK 102 PA6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Ultramid 8351 HS BK-102 is a heat stabilized, pigmented black, impact modified type 6 nylon graft copolymer developed for injection molding applications requiring a high level of toughness combined with a moderate flexibility and faster cycles. Excellent thermal and chemical resistance properties provided by the nylon backbone. It demonstrates the highest impact performance within the Ultramid copolymer product line while maintaining an excellent balance of strength and stiffness. Excellent chemical resistance to greases, oils and hydrocarbons.Applications: Ultramid 8351 HS BK-102 is generally recommended for applications such as spray gun and power tool handles, trim clips and fasteners, wall anchors and automotive roof clips rack components.Information provided by BASF
Physical Properties Metric English Comments
Density 1.07 g/cc
0.0387 lb/in³
ASTM D792
Moisture Absorption at Equilibrium 1.1 %
1.1 %
24 Hours; ASTM D570
1.9 %
1.9 %
50% RH; ASTM D570
6.7 %
6.7 %
Saturation; ASTM D570
Linear Mold Shrinkage 0.03556 cm/cm
0.03556 in/in
1/8" bar
Mechanical Properties Metric English Comments
Hardness, Rockwell R 78
78
ASTM D785
Tensile Strength, Yield 55.0 MPa
7980 psi
ASTM D638
Elongation at Break >= 100 %
>= 100 %
ASTM D638
Elongation at Yield 5.0 %
5.0 %
ASTM D638
Flexural Strength 66.0 MPa
9570 psi
ASTM D790
Flexural Modulus 1.69 GPa
245 ksi
ASTM D790
Izod Impact, Notched (ISO) NB
NB
ASTM D256
Dart Drop, Total Energy 285 J
210 ft-lb
BASF
Thermal Properties Metric English Comments
CTE, linear 106 µm/m-°C
58.9 µin/in-°F
ASTM E831
Melting Point 220 °C
428 °F
ASTM D3418
Deflection Temperature at 1.8 MPa (264 psi) 55.0 °C
131 °F
ASTM D648
UL RTI, Electrical 105 °C

@Thickness 1.50 mm
221 °F

@Thickness 0.0591 in
746B
UL RTI, Mechanical with Impact 105 °C

@Thickness 1.50 mm
221 °F

@Thickness 0.0591 in
746B
UL RTI, Mechanical without Impact 105 °C

@Thickness 1.50 mm
221 °F

@Thickness 0.0591 in
746B
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
ASTM D257
Processing Properties Metric English Comments
Melt Temperature 240 - 270 °C
464 - 518 °F
Mold Temperature 80.0 - 95.0 °C
176 - 203 °F
Dry Time 2 - 4 hour
2 - 4 hour
Moisture Content <= 0.20 %
<= 0.20 %
Descriptive Properties Value Comments
Color BK 102
Commercial Status North America