BASF Ultramid® 8350 HS PA6 (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® 8350 HS PA6 (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultramid 8350 HS is a heat stabilized, impact modified type 6 graft copolymer developed for extrusion, tubing, and jacketing applications requiring a high level of toughness combined with a moderate level of flexibility. It is also available in non-heat stabilized (Ultramid 8350) and/or pigmented versions.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | dry; ISO 1183 |
| Water Absorption | 1.1 % | 1.1 % | 24 hour; ISO Test |
| 6.7 % | 6.7 % | beginning dry; ISO 62 | |
| Moisture Absorption at Equilibrium | 1.9 % | 1.9 % | beginning dry (23°C/50% R.H.); ISO 62 |
| Linear Mold Shrinkage | 0.014 cm/cm | 0.014 in/in | ASTM Data; MD |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | 2 in/min; ASTM Test |
| 32.0 MPa | 4640 psi | 50mm/min; ISO 527 | |
| 95.0 MPa @Temperature -40.0 °C |
13800 psi @Temperature -40.0 °F |
ISO Data | |
| 95.0 MPa @Temperature -40.0 °C |
13800 psi @Temperature -40.0 °F |
ASTM Test | |
| Elongation at Break | >= 50 % | >= 50 % | 50mm/min, Nominal strain; ISO 527 |
| >= 100 % | >= 100 % | 2 in/min; ASTM Test | |
| Elongation at Yield | 9.0 % | 9.0 % | 50mm/min; ISO 527 |
| 9.0 % | 9.0 % | 2 in/min; ASTM Test | |
| Tensile Modulus | 0.675 GPa | 97.9 ksi | 1mm/min; ISO 527 |
| Flexural Strength | 30.0 MPa | 4350 psi | ASTM Test |
| 120 MPa @Temperature -40.0 °C |
17400 psi @Temperature -40.0 °F |
ASTM Test | |
| Flexural Modulus | 0.620 GPa | 89.9 ksi | ASTM Test |
| Izod Impact, Notched | 1.55 J/cm @Temperature -40.0 °C |
2.90 ft-lb/in @Temperature -40.0 °F |
ASTM Test |
| NB @Thickness 3.17 mm |
NB @Thickness 0.125 in |
ASTM Test |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | 10 K/min |
| 220 °C | 428 °F | ASTM Test |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 °C | 536 °F | Injection molding |
| Mold Temperature | 70.0 °C | 158 °F | Injection molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural | |
| Commercial Status | Active America | |
| Form | Pellets | |
| Impact Modified | Yes | |
| Primary Processing Technique | Extrusion | |
| Processing | Injection Molding | |
| Other Extrusion | ||
| Profile extrusion | ||
| Special characteristic | Heat stabilized or stable to heat | |
| UL.UL-C | Yes |