BASF Ultramid® 8350 HS BK-102 PA6 (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade
Manufacturer BASF
Trade Name Ultramid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® 8350 HS BK-102 PA6 (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid 8350 HS BK-102 is a type 6, black pigmented, impact modified graft copolymer developed for extrusion, tubing, and jacketing applications requiring a high level of toughness combined with a moderate level of flexibility.
Physical Properties Metric English Comments
Density 1.07 g/cc
0.0387 lb/in³
dry; ISO 1183
Water Absorption 1.1 %
1.1 %
24 hour; ISO Test
6.7 %
6.7 %
beginning dry; ISO 62
Moisture Absorption at Equilibrium 1.9 %
1.9 %
beginning dry (23°C/50% R.H.); ISO 62
Linear Mold Shrinkage 0.014 cm/cm
0.014 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Tensile Strength, Yield 32.0 MPa
4640 psi
50mm/min; ISO 527
32.0 MPa
4640 psi
2 in/min; ASTM Test
Elongation at Break >= 50 %
>= 50 %
50mm/min, Nominal strain; ISO 527
>= 100 %
>= 100 %
2 in/min; ASTM Test
Elongation at Yield 9.0 %
9.0 %
50mm/min; ISO 527
9.0 %
9.0 %
2 in/min; ASTM Test
Tensile Modulus 0.675 GPa
97.9 ksi
1mm/min; ISO 527
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
10 K/min
220 °C
428 °F
ASTM Test
Processing Properties Metric English Comments
Melt Temperature 280 °C
536 °F
Injection molding
Mold Temperature 70.0 °C
158 °F
Injection molding
Descriptive Properties Value Comments
Color BK-102
Commercial Status Active America
Form Pellets
Impact Modified Yes
Primary Processing Technique Extrusion
Processing Injection Molding
Other Extrusion
Profile extrusion
Special characteristic Heat stabilized or stable to heat
UL.UL-C Yes