BASF Ultramid® 8333G HI HS BK-102 33% Glass Filled PA6 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® 8333G HI HS BK-102 33% Glass Filled PA6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid 8333G HI HS BK-102 is a 33% glass reinforced, heat stabilized, impact modified, pigmented black, PA6 injection molding compound developed for applications requiring improved dry as molded toughness in combination with a balance of strength, stiffness and excellent moldability/surface aesthetics. It is also available in heat stabilized (Ultramid 8333G HI HS) and/or pigmented versions.
Physical Properties Metric English Comments
Density 1.34 g/cc
0.0484 lb/in³
ISO 1183
Water Absorption 0.90 %
0.90 %
24 hour; ISO Test
5.5 %
5.5 %
ISO 62
Moisture Absorption at Equilibrium 1.5 %
1.5 %
23°C/50% R.H.; ISO 62
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Hardness, Rockwell R 121
121
ASTM Test
Tensile Strength at Break 150 MPa
21800 psi
0.2 in/min; ASTM Test
Tensile Strength, Ultimate 140 MPa
20300 psi
5mm/min; ISO 527
Elongation at Break 3.0 %
3.0 %
5mm/min; ISO 527
3.0 %
3.0 %
0.2 in/min; ASTM Test
Tensile Modulus 9.10 GPa
1320 ksi
1mm/min; ISO 527
Flexural Strength 210 MPa
30500 psi
ISO Data
240 MPa
34800 psi
ASTM Test
Flexural Modulus 7.50 GPa
1090 ksi
ISO Data
8.14 GPa
1180 ksi
ASTM Test
Izod Impact, Notched 1.05 J/cm

@Temperature -40.0 °C
1.97 ft-lb/in

@Temperature -40.0 °F
ASTM Test
2.10 J/cm

@Thickness 3.17 mm
3.93 ft-lb/in

@Thickness 0.125 in
ASTM Test
Izod Impact, Notched (ISO) 19.0 kJ/m²
9.04 ft-lb/in²
ISO Test
13.0 kJ/m²

@Temperature -40.0 °C
6.19 ft-lb/in²

@Temperature -40.0 °F
ISO Test
Charpy Impact Unnotched 7.10 J/cm²
33.8 ft-lb/in²
ISO 179
Charpy Impact, Notched 1.80 J/cm²
8.57 ft-lb/in²
ISO 179
1.00 J/cm²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
ISO 179
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
10 K/min
220 °C
428 °F
ASTM Test
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 205 °C
401 °F
ISO 75
210 °C
410 °F
ASTM Test
Flammability, UL94 HB

@Thickness 0.800 mm
HB

@Thickness 0.0315 in
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
Descriptive Properties Value Comments
Color BK-102
Commercial Status Active America
Impact Modified Yes
Primary Processing Technique Injection Molding
UL.UL-C Yes