BASF Ultramid® 8270 HS BK 102 PA6 (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® 8270 HS BK 102 PA6 (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Ultramid 8270 HS BK-102 is a thermally modified pigmented black, PA6 blow molding compound exhibiting exceptional toughness and melt strength ideally suited for blow molding, profile extrusion, and other applications requiring extra high melt viscosity. It exhibits excellent permeability and chemical resistance to oils, hydrocarbons and most solvents.Applications: Industrial containers, small gasoline tanks, and automotive under hood reservoirs.Information provided by BASF
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792 |
| Moisture Absorption at Equilibrium | 1.6 % | 1.6 % | 24 Hours; ASTM D570 |
| 2.6 % | 2.6 % | 50% RH; ASTM D570 | |
| 9.2 % | 9.2 % | Saturation; ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 99 | 99 | ASTM D785 |
| Tensile Strength, Yield | 24.0 MPa @Temperature 121 °C |
3480 psi @Temperature 250 °F |
ASTM D638 |
| 84.0 MPa @Temperature 23.0 °C |
12200 psi @Temperature 73.4 °F |
ASTM D638 | |
| 138 MPa @Temperature -40.0 °C |
20000 psi @Temperature -40.0 °F |
ASTM D638 | |
| Elongation at Break | >= 100 % | >= 100 % | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Strength | 17.0 MPa @Temperature 121 °C |
2470 psi @Temperature 250 °F |
ASTM D790 |
| 20.0 MPa @Temperature 90.0 °C |
2900 psi @Temperature 194 °F |
ASTM D790 | |
| 30.0 MPa @Temperature 65.0 °C |
4350 psi @Temperature 149 °F |
ASTM D790 | |
| 114 MPa @Temperature 23.0 °C |
16500 psi @Temperature 73.4 °F |
ASTM D790 | |
| 179 MPa @Temperature -40.0 °C |
26000 psi @Temperature -40.0 °F |
ASTM D790 | |
| Flexural Modulus | 0.260 GPa @Temperature 121 °C |
37.7 ksi @Temperature 250 °F |
ASTM D790 |
| 0.310 GPa @Temperature 90.0 °C |
45.0 ksi @Temperature 194 °F |
ASTM D790 | |
| 0.435 GPa @Temperature 65.0 °C |
63.1 ksi @Temperature 149 °F |
ASTM D790 | |
| 2.90 GPa @Temperature 23.0 °C |
421 ksi @Temperature 73.4 °F |
ASTM D790 | |
| 3.16 GPa @Temperature -40.0 °C |
458 ksi @Temperature -40.0 °F |
ASTM D790 | |
| Izod Impact, Notched | 0.530 J/cm @Temperature -40.0 °C |
0.993 ft-lb/in @Temperature -40.0 °F |
ASTM D256 |
| 0.530 J/cm @Temperature 23.0 °C |
0.993 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 135 µm/m-°C | 75.0 µin/in-°F | ASTM E831 |
| Melting Point | 220 °C | 428 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 169 °C | 336 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 63.0 °C | 145 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 245 - 260 °C | 473 - 500 °F | |
| Mold Temperature | 60.0 °C | 140 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Moisture Content | <= 0.15 % | <= 0.15 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | BK 102 | |
| Commercial Status | North America |