BASF Ultramid® 8266G HS BK-102 15/25% Glass/Mineral Filled PA6 (Dry)

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass/Mineral Reinforced
Manufacturer	BASF
Trade Name	Ultramid®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultramid® 8266G HS BK-102 15/25% Glass/Mineral Filled PA6 (Dry).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Ultramid 8266G HS is a heat stabilized, 40% glass and mineral reinforced nylon 6 injection molding compound resulting in a balance of engineering properties with excellent dimensional stability, low warp and good resistance to sink mark formation. It exhibits high strength, rigidity, and heat distortion temperature. Its resistance to creep under load is excellent. It maintains its inherent chemical resistance to greases, oils and hydrocarbons.

Physical Properties	Metric	English	Comments
Water Absorption	1.3 %	1.3 %	24 hour; ISO Test
Linear Mold Shrinkage	0.0040 cm/cm	0.0040 in/in	ASTM Data; MD

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	119	119	ASTM Test
Tensile Strength at Break	130 MPa	18900 psi	0.2 in/min; ASTM Test
Elongation at Break	2.5 %	2.5 %	0.2 in/min; ASTM Test
Izod Impact, Notched	0.530 J/cm @Thickness 3.17 mm	0.993 ft-lb/in @Thickness 0.125 in	ASTM Test
Izod Impact, Notched (ISO)	5.80 kJ/m²	2.76 ft-lb/in²	ISO Test

Thermal Properties	Metric	English	Comments
CTE, linear	31.0 µm/m-°C @Temperature -30.0 - 30.0 °C	17.2 µin/in-°F @Temperature -22.0 - 86.0 °F	ASTM Test

Descriptive Properties	Value	Comments
Color	BK-102
Commercial Status	Active America
Impact Modified	No
Primary Processing Technique	Injection Molding
UL.UL-C	Yes