BASF Ultramid® 8260 HS BK-102 40% Mineral Filled PA6 (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Mineral Filled
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® 8260 HS BK-102 40% Mineral Filled PA6 (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid 8260 HS BK-102 is a heat stabilized, pigmented black, 40% mineral reinforced PA6 injection molding resin. It possesses high stiffness, dimensional stability and heat resistance combined with excellent processability including low warp and resistance to sink-mark formation. It maintains its inherent chemical resistance to greases, oils and hydrocarbons.
Physical Properties Metric English Comments
Density 1.49 g/cc
0.0538 lb/in³
dry; ISO 1183
Water Absorption 1.1 %
1.1 %
24 hour; ISO Test
5.7 %
5.7 %
beginning dry; ISO 62
Moisture Absorption at Equilibrium 1.6 %
1.6 %
beginning dry (23°C/50% R.H.); ISO 62
Linear Mold Shrinkage 0.0090 cm/cm
0.0090 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Tensile Strength at Break 60.0 MPa
8700 psi
0.2 in/min; ASTM Test
27.0 MPa

@Temperature 120 °C
3920 psi

@Temperature 248 °F
ISO Data
27.0 MPa

@Temperature 120 °C
3920 psi

@Temperature 248 °F
ASTM Test
35.0 MPa

@Temperature 80.0 °C
5080 psi

@Temperature 176 °F
ASTM Test
35.0 MPa

@Temperature 80.0 °C
5080 psi

@Temperature 176 °F
ISO Data
135 MPa

@Temperature -40.0 °C
19600 psi

@Temperature -40.0 °F
ASTM Test
135 MPa

@Temperature -40.0 °C
19600 psi

@Temperature -40.0 °F
ISO Data
Tensile Strength, Ultimate 60.0 MPa
8700 psi
5mm/min; ISO 527
Elongation at Break 30 %
30 %
5mm/min; ISO 527
30 %
30 %
0.2 in/min; ASTM Test
5.0 %

@Temperature -40.0 °C
5.0 %

@Temperature -40.0 °F
ASTM Test
5.0 %

@Temperature -40.0 °C
5.0 %

@Temperature -40.0 °F
ISO Data
30 %

@Temperature 80.0 °C
30 %

@Temperature 176 °F
ASTM Test
30 %

@Temperature 80.0 °C
30 %

@Temperature 176 °F
ISO Data
40 %

@Temperature 120 °C
40 %

@Temperature 248 °F
ASTM Test
40 %

@Temperature 120 °C
40 %

@Temperature 248 °F
ISO Data
Tensile Modulus 3.80 GPa
551 ksi
1mm/min; ISO 527
1.20 GPa

@Temperature 120 °C
174 ksi

@Temperature 248 °F
ISO Data
1.40 GPa

@Temperature 80.0 °C
203 ksi

@Temperature 176 °F
ISO Data
7.70 GPa

@Temperature -40.0 °C
1120 ksi

@Temperature -40.0 °F
ISO Data
Flexural Strength 50.0 MPa
7250 psi
ISO Data
Flexural Modulus 2.10 GPa
305 ksi
ISO Data
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
10 K/min
220 °C
428 °F
ASTM Test
Processing Properties Metric English Comments
Melt Temperature 275 °C
527 °F
Injection molding
Mold Temperature 95.0 °C
203 °F
Injection molding
Descriptive Properties Value Comments
Color BK-102
Commercial Status Active America
Form Pellets
Impact Modified No
Primary Processing Technique Injection Molding
Processing Injection Molding
Special characteristic Heat stabilized or stable to heat
X
UL.UL-C Yes