BASF Ultramid® 8253 PA6 (Conditioned)

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade
Manufacturer	BASF
Trade Name	Ultramid®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultramid® 8253 PA6 (Conditioned).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Ultramid 8253 is an unfilled, impact modified type 6 graft copolymer developed for both injection molding and extrusion applications. It is also available in heat stabilized (Ultramid 8253 HS) and/or pigmented versions. Copolymerization results in improved dry as molded toughness and increased flexibility to meet higher impact performance compared to conventional unreinforced homopolymers. Good nylon thermal and chemical properties are maintained along with good strength and stiffness retention.

Physical Properties	Metric	English	Comments
Density	1.09 g/cc	0.0394 lb/in³	dry; ISO 1183
Water Absorption	1.5 %	1.5 %	24 hour; ISO Test
	8.1 %	8.1 %	beginning dry; ISO 62
Moisture Absorption at Equilibrium	2.3 %	2.3 %	beginning dry (23°C/50% R.H.); ISO 62
Linear Mold Shrinkage	0.012 cm/cm	0.012 in/in	ASTM Data; MD

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	70.0 MPa @Temperature -40.0 °C	10200 psi @Temperature -40.0 °F	ISO Data
	70.0 MPa @Temperature -40.0 °C	10200 psi @Temperature -40.0 °F	ASTM Test
Tensile Strength, Yield	32.0 MPa	4640 psi	50mm/min; ISO 527
	32.0 MPa	4640 psi	2 in/min; ASTM Test
	20.0 MPa @Temperature 80.0 °C	2900 psi @Temperature 176 °F	ASTM Test
	20.0 MPa @Temperature 80.0 °C	2900 psi @Temperature 176 °F	ISO Data
	116 MPa @Temperature -40.0 °C	16800 psi @Temperature -40.0 °F	ASTM Test
	116 MPa @Temperature -40.0 °C	16800 psi @Temperature -40.0 °F	ISO Data
Elongation at Break	>= 50 %	>= 50 %	50mm/min, Nominal strain; ISO 527
	>= 100 %	>= 100 %	2 in/min; ASTM Test
	20 % @Temperature -40.0 °C	20 % @Temperature -40.0 °F	ASTM Test
	20 % @Temperature -40.0 °C	20 % @Temperature -40.0 °F	ISO Data
Elongation at Yield	15 %	15 %	2 in/min; ASTM Test
	15 %	15 %	50mm/min; ISO 527
	30 % @Temperature 80.0 °C	30 % @Temperature 176 °F	ISO Data
	30 % @Temperature 120 °C	30 % @Temperature 248 °F	ASTM Test
Tensile Modulus	0.730 GPa	106 ksi	1mm/min; ISO 527
	0.220 GPa @Temperature 120 °C	31.9 ksi @Temperature 248 °F	ISO Data
	0.370 GPa @Temperature 80.0 °C	53.7 ksi @Temperature 176 °F	ISO Data
	3.30 GPa @Temperature -40.0 °C	479 ksi @Temperature -40.0 °F	ISO Data
Flexural Strength	32.0 MPa	4640 psi	ASTM Test
	141 MPa @Temperature -40.0 °C	20500 psi @Temperature -40.0 °F	ASTM Test
Flexural Modulus	0.670 GPa	97.2 ksi	ASTM Test
Izod Impact, Notched	0.640 J/cm @Temperature -40.0 °C	1.20 ft-lb/in @Temperature -40.0 °F	ASTM Test
	NB @Thickness 3.17 mm	NB @Thickness 0.125 in	ASTM Test

Thermal Properties	Metric	English	Comments
Melting Point	220 °C	428 °F	10 K/min
	220 °C	428 °F	ASTM Test

Processing Properties	Metric	English	Comments
Melt Temperature	280 °C	536 °F	Injection molding
Mold Temperature	70.0 °C	158 °F	Injection molding

Descriptive Properties	Value	Comments
Color	Natural
Commercial Status	Active America
Form	Pellets
Impact Modified	Yes
Primary Processing Technique	Injection Molding
Processing	Injection Molding
UL.UL-C	Yes