BASF Ultramid® 8234G HS 44% Glass Filled PA6 (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® 8234G HS 44% Glass Filled PA6 (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid 8234G HS is a heat stabilized, 44% glass fiber reinforced polyamide 6 injection molding compound offering the highest level of strength, stiffness, high temperature performance and dimensional stability. It is available in natural, black, weather resistance and pigmented versions.
Physical Properties Metric English Comments
Density 1.2784 g/cc
0.046185 lb/in³
Melt; ISO 1183
1.49 g/cc
0.0538 lb/in³
dry; ISO 1183
Water Absorption 0.90 %
0.90 %
24 hour; ISO Test
5.2 %
5.2 %
beginning dry; ISO 62
Moisture Absorption at Equilibrium 1.5 %
1.5 %
beginning dry (23°C/50% R.H.); ISO 62
Relative Viscosity 2.6 cP
2.6 cP
ISO Test; 96 % SAV
Viscosity Measurement 50
50
Formic Acid
Linear Mold Shrinkage 0.0020 cm/cm
0.0020 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Tensile Strength at Break 145 MPa
21000 psi
0.2 in/min; ASTM Test
Tensile Strength, Ultimate 145 MPa
21000 psi
5mm/min; ISO 527
Elongation at Break 6.0 %
6.0 %
5mm/min; ISO 527
6.0 %
6.0 %
0.2 in/min; ASTM Test
Tensile Modulus 7.49 GPa
1090 ksi
1mm/min; ISO 527
Flexural Strength 212 MPa
30700 psi
ASTM Test
410 MPa

@Temperature -40.0 °C
59500 psi

@Temperature -40.0 °F
ASTM Test
Flexural Modulus 6.56 GPa
951 ksi
ASTM Test
Thermal Properties Metric English Comments
Specific Heat Capacity 2.522 J/g-°C
0.6028 BTU/lb-°F
Melt
Thermal Conductivity 0.329 W/m-K
2.28 BTU-in/hr-ft²-°F
Melt
Melting Point 220 °C
428 °F
10 K/min
220 °C
428 °F
ASTM Test
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
IEC 60093
Comparative Tracking Index 500 V
500 V
IEC 60112
Descriptive Properties Value Comments
Color Natural
Commercial Status Active America
Form Pellets
Impact Modified No
Primary Processing Technique Injection Molding
Processing Injection Molding
Special characteristic Heat stabilized or stable to heat
UL.UL-C Yes