BASF Ultramid® 8233G HS BK-106 33% Glass Filled PA6 (Conditioned)

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer	BASF
Trade Name	Ultramid®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultramid® 8233G HS BK-106 33% Glass Filled PA6 (Conditioned).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Ultramid 8233G HS BK-106 is a heat stabilized, weather resistant, 33% glass fiber reinforced PA6 injection molding compound offering excellent strength, stiffness, high temperature performance and dimensional stability. This balance of engineering properties in combination with excellent processability make it ideal in applications replacing metal, resulting in an overall cost and weight savings.

Physical Properties	Metric	English	Comments
Density	1.39 g/cc	0.0502 lb/in³	dry; ISO 1183
Water Absorption	1.1 %	1.1 %	24 hour; ISO Test
	6.4 %	6.4 %	beginning dry; ISO 62
Moisture Absorption at Equilibrium	1.8 %	1.8 %	beginning dry (23°C/50% R.H.); ISO 62
Relative Viscosity	2.6 cP	2.6 cP	ISO Test; 96 % SAV
Viscosity Measurement	50	50	Formic Acid
Linear Mold Shrinkage	0.0030 cm/cm	0.0030 in/in	ASTM Data; MD

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	100 MPa	14500 psi	0.2 in/min; ASTM Test
	60.0 MPa @Temperature 120 °C	8700 psi @Temperature 248 °F	ISO Data
	60.0 MPa @Temperature 120 °C	8700 psi @Temperature 248 °F	ASTM Test
	70.0 MPa @Temperature 80.0 °C	10200 psi @Temperature 176 °F	ASTM Test
	70.0 MPa @Temperature 80.0 °C	10200 psi @Temperature 176 °F	ISO Data
	215 MPa @Temperature -40.0 °C	31200 psi @Temperature -40.0 °F	ASTM Test
	215 MPa @Temperature -40.0 °C	31200 psi @Temperature -40.0 °F	ISO Data
Tensile Strength, Ultimate	100 MPa	14500 psi	5mm/min; ISO 527
Elongation at Break	6.0 %	6.0 %	0.2 in/min; ASTM Test
	6.0 %	6.0 %	5mm/min; ISO 527
	2.5 % @Temperature -40.0 °C	2.5 % @Temperature -40.0 °F	ISO Data
	2.5 % @Temperature -40.0 °C	2.5 % @Temperature -40.0 °F	ASTM Test
	6.5 % @Temperature 120 °C	6.5 % @Temperature 248 °F	ASTM Test
	6.5 % @Temperature 80.0 °C	6.5 % @Temperature 176 °F	ASTM Test
	6.5 % @Temperature 120 °C	6.5 % @Temperature 248 °F	ISO Data
	6.5 % @Temperature 80.0 °C	6.5 % @Temperature 176 °F	ISO Data
Tensile Modulus	7.70 GPa	1120 ksi	1mm/min; ISO 527
	4.20 GPa @Temperature 120 °C	609 ksi @Temperature 248 °F	ISO Data
	4.60 GPa @Temperature 80.0 °C	667 ksi @Temperature 176 °F	ISO Data
	11.5 GPa @Temperature -40.0 °C	1670 ksi @Temperature -40.0 °F	ISO Data

Thermal Properties	Metric	English	Comments
Melting Point	220 °C	428 °F	10 K/min
	220 °C	428 °F	ASTM Test

Processing Properties	Metric	English	Comments
Melt Temperature	275 °C	527 °F	Injection molding
Mold Temperature	95.0 °C	203 °F	Injection molding

Descriptive Properties	Value	Comments
Color	BK-106
Commercial Status	Active America
Form	Pellets
Impact Modified	No
Primary Processing Technique	Injection Molding
Processing	Injection Molding
Special characteristic	Heat stabilized or stable to heat
UL.UL-C	Yes