BASF Ultramid® 8232G HS FR 25% Glass Fiber Fire Retardant PA6 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled , Nylon 6, Glass Fiber Filled, Flame Retardant
Manufacturer BASF
Trade Name Ultramid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® 8232G HS FR 25% Glass Fiber Fire Retardant PA6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Ultramid 8232G HS FR is a 25% glass fiber reinforced, heat stabilized, flame retardant PA6 injection molding compound exhibiting excellent melt stability characteristics. It combines flame retardant ability with an excellent balance of high strength, stiffness and heat distortion temperature.Applications: connectors, terminal blocks, switches and receptacles, coil bobbins, and appliance housingInformation provided by BASF
Physical Properties Metric English Comments
Density 1.62 g/cc
0.0585 lb/in³
ASTM D792
Moisture Absorption at Equilibrium 0.90 %
0.90 %
24 hour; ASTM D570
1.1 %
1.1 %
50% RH; ASTM D570
4.0 %
4.0 %
Saturation; ASTM D570
Linear Mold Shrinkage 0.00762 cm/cm
0.00762 in/in
1/8" bar
Mechanical Properties Metric English Comments
Hardness, Rockwell R 121
121
ASTM D785
Tensile Strength at Break 157 MPa
22800 psi
ASTM D638
Elongation at Break 3.0 %
3.0 %
ASTM D638
Flexural Strength 232 MPa
33600 psi
ASTM D790
Flexural Modulus 8.97 GPa
1300 ksi
ASTM D790
Izod Impact, Notched (ISO) 107 kJ/m²
50.9 ft-lb/in²
ASTM D256
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
ASTM D3418
Deflection Temperature at 1.8 MPa (264 psi) 195 °C
383 °F
ASTM D684
UL RTI, Electrical 130 °C

@Thickness 1.50 mm
266 °F

@Thickness 0.0591 in
746B
UL RTI, Mechanical with Impact 115 °C

@Thickness 1.50 mm
239 °F

@Thickness 0.0591 in
746B
UL RTI, Mechanical without Impact 115 °C

@Thickness 1.50 mm
239 °F

@Thickness 0.0591 in
746B
Flammability, UL94 V-0

@Thickness >=1.50 mm
V-0

@Thickness >=0.0591 in
V-0

@Thickness >=2.50 mm
V-0

@Thickness >=0.0984 in
5VB

@Thickness >=2.50 mm
5VB

@Thickness >=0.0984 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
ASTM D257
Dielectric Strength 29.0 kV/mm
737 kV/in
ASTM D149
Processing Properties Metric English Comments
Melt Temperature 250 - 290 °C
482 - 554 °F
Mold Temperature 80.0 - 95.0 °C
176 - 203 °F
Dry Time 2 - 4 hour
2 - 4 hour
Moisture Content <= 0.15 %
<= 0.15 %
Descriptive Properties Value Comments
Color White to gray
Commercial Status North America