BASF Ultramid® 8231G HS BK-102 14% Glass Filled PA6 (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 10% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® 8231G HS BK-102 14% Glass Filled PA6 (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid 8231G HS BK-102 is a black pigmented heat stabilized, 14% glass fiber reinforced PA6 injection molding compound.The glass fiber reinforcement enhances performance such as strength, stiffness and heat deflection temperature. The heat stabilizer system extends the properties at elevated temperatures. It also has excellent chemical resistance to greases, oils and hydrocarbons.
Physical Properties Metric English Comments
Density 1.23 g/cc
0.0444 lb/in³
dry; ISO 1183
Water Absorption 1.4 %
1.4 %
24 hour; ISO Test
8.1 %
8.1 %
beginning dry; ISO 62
Moisture Absorption at Equilibrium 2.3 %
2.3 %
beginning dry (23°C/50% R.H.); ISO 62
Relative Viscosity 2.6 cP
2.6 cP
ISO Test; 96 % SAV
Viscosity Measurement 50
50
Formic Acid
Linear Mold Shrinkage 0.0050 cm/cm
0.0050 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Tensile Strength at Break 60.0 MPa
8700 psi
0.2 in/min; ASTM Test
30.0 MPa

@Temperature 80.0 °C
4350 psi

@Temperature 176 °F
ISO Data
30.0 MPa

@Temperature 80.0 °C
4350 psi

@Temperature 176 °F
ASTM Test
40.0 MPa

@Temperature 120 °C
5800 psi

@Temperature 248 °F
ASTM Test
40.0 MPa

@Temperature 120 °C
5800 psi

@Temperature 248 °F
ISO Data
150 MPa

@Temperature -40.0 °C
21800 psi

@Temperature -40.0 °F
ISO Data
150 MPa

@Temperature -40.0 °C
21800 psi

@Temperature -40.0 °F
ASTM Test
Tensile Strength, Ultimate 60.0 MPa
8700 psi
5mm/min; ISO 527
Elongation at Break 20 %
20 %
5mm/min; ISO 527
20 %
20 %
0.2 in/min; ASTM Test
3.0 %

@Temperature -40.0 °C
3.0 %

@Temperature -40.0 °F
ASTM Test
3.0 %

@Temperature -40.0 °C
3.0 %

@Temperature -40.0 °F
ISO Data
9.0 %

@Temperature 120 °C
9.0 %

@Temperature 248 °F
ISO Data
9.0 %

@Temperature 120 °C
9.0 %

@Temperature 248 °F
ASTM Test
15 %

@Temperature 80.0 °C
15 %

@Temperature 176 °F
ASTM Test
15 %

@Temperature 80.0 °C
15 %

@Temperature 176 °F
ISO Data
Tensile Modulus 3.10 GPa
450 ksi
1mm/min; ISO 527
1.80 GPa

@Temperature 120 °C
261 ksi

@Temperature 248 °F
ISO Data
2.30 GPa

@Temperature 80.0 °C
334 ksi

@Temperature 176 °F
ISO Data
6.90 GPa

@Temperature -40.0 °C
1000 ksi

@Temperature -40.0 °F
ISO Data
Flexural Strength 65.0 MPa
9430 psi
ISO Data
Flexural Modulus 2.21 GPa
321 ksi
ISO Data
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
10 K/min
220 °C
428 °F
ASTM Test
Processing Properties Metric English Comments
Melt Temperature 275 °C
527 °F
Injection molding
Mold Temperature 95.0 °C
203 °F
Injection molding
Descriptive Properties Value Comments
Color BK-102
Commercial Status Active America
Form Pellets
Impact Modified No
Primary Processing Technique Injection Molding
Processing Injection Molding
Special characteristic Heat stabilized or stable to heat
UL.UL-C Yes