BASF Ultramid® 8202CQ PA6 (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced
Manufacturer BASF
Trade Name Ultramid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® 8202CQ PA6 (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid 8202CQ is a low viscosity, PA6 injection molding homopolymer, possessing a modified crystalline structure or increased property performance and faster cycles. It is also available in pigmented versions.
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
dry; ISO 1183
Water Absorption 1.6 %
1.6 %
24 hour; ISO Test
9.2 %
9.2 %
beginning dry; ISO 62
Moisture Absorption at Equilibrium 2.6 %
2.6 %
beginning dry (23°C/50% R.H.); ISO 62
Relative Viscosity 2.6 cP
2.6 cP
ISO Test; 96 % SAV
Viscosity Measurement 48
48
Formic Acid
Linear Mold Shrinkage 0.010 cm/cm
0.010 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Tensile Strength, Yield 43.0 MPa
6240 psi
2 in/min; ASTM Test
43.0 MPa
6240 psi
50mm/min; ISO 527
142 MPa

@Temperature -40.0 °C
20600 psi

@Temperature -40.0 °F
ISO Data
142 MPa

@Temperature -40.0 °C
20600 psi

@Temperature -40.0 °F
ASTM Test
Elongation at Break >= 50 %
>= 50 %
50mm/min, Nominal strain; ISO 527
>= 100 %
>= 100 %
2 in/min; ASTM Test
Elongation at Yield 14 %
14 %
50mm/min; ISO 527
14 %
14 %
2 in/min; ASTM Test
3.0 %

@Temperature -40.0 °C
3.0 %

@Temperature -40.0 °F
ISO Data
Tensile Modulus 1.22 GPa
177 ksi
1mm/min; ISO 527
Flexural Strength 29.0 MPa
4210 psi
ISO Data
42.0 MPa
6090 psi
ASTM Test
168 MPa

@Temperature -40.0 °C
24400 psi

@Temperature -40.0 °F
ASTM Test
Flexural Modulus 0.970 GPa
141 ksi
ASTM Test
1.01 GPa
146 ksi
ISO Data
Izod Impact, Notched 0.210 J/cm

@Temperature -40.0 °C
0.393 ft-lb/in

@Temperature -40.0 °F
ASTM Test
1.60 J/cm

@Thickness 3.17 mm
3.00 ft-lb/in

@Thickness 0.125 in
ASTM Test
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
10 K/min
220 °C
428 °F
ASTM Test
Processing Properties Metric English Comments
Melt Temperature 260 °C
500 °F
Injection molding
Mold Temperature 80.0 °C
176 °F
Injection molding
Descriptive Properties Value Comments
Color Natural
Commercial Status Active America
Form Pellets
Impact Modified No
Primary Processing Technique Injection Molding
Processing Injection Molding
UL.UL-C Yes